The invention discloses a high-life marble cutter head carcass and a manufacturing method thereof. The formula component is composed of the following weight percentage: Cu \u2011 Sn \u2011 Si alloy 15 \u2011 25%; Cu \u2011 Zn alloy 10 \u2011 20%; ni10 \u2011 20%; Cu \u2011 Sn alloy 35 \u2011 65%. Through the introduction of specific new materials and the reasonable configuration of each component, the matrix of the cutter head of the invention can be more reasonable fused in brittleness, wear resistance and toughness, effectively enhancing the universality of the matrix, making the diamond cutter head suitable for cutting various types of marble, and improving the service life of 20 \u2011 30% while maintaining the sharpness.
【技术实现步骤摘要】
一种高寿命大理石刀头胎体及刀头制作方法
本专利技术涉及金刚石刀头
，具体是指一种高寿命大理石刀头胎体及刀头制作方法。
技术介绍
目前大理石刀头胎体配方主要有两大类，一类只有Cu、Sn两种元素，这类胎体硬脆，耐磨度低，切割时锋利好，但是寿命低。另一类是在第一类胎体基础上添加Fe元素，Fe的性能质软，的加入确实可以提高耐磨性,增加寿命,但是在切割一些硬大理石时,金刚石出露慢,金刚石刀头的通用性降低。鉴于此，本案专利技术人对上述问题进行深入研究，并提出一种高寿命大理石刀头胎体及刀头制作方法，本案由此产生。
技术实现思路
本专利技术的目的在于提供一种高寿命大理石刀头胎体及刀头制作方法，为了达成上述目的，本专利技术的解决方案是：一种高寿命大理石刀头胎体，配方组分由如下重量百分比组成：所述配方中，组分的粉末粒度范围为200-500目，氧含量在1500—3500PPM。所述Cu-Sn-Si合金中各成分重量占比为：Si1％,Sn15％,Cu84％。所述Cu-Z...
【技术保护点】
1.一种高寿命大理石刀头胎体，其特征在于，配方组分由如下重量百分比组成：/n
【技术特征摘要】
1.一种高寿命大理石刀头胎体，其特征在于，配方组分由如下重量百分比组成：
2.如权利要求1所述的一种高寿命大理石刀头胎体，其特征在于，所述配方中，组分的粉末粒度范围为200-500目，氧含量在1500—3500PPM。
3.如权利要求1所述的一种高寿命大理石刀头胎体，其特征在于，所述Cu-Sn-Si合金中各成分重量占比为：Si1％,Sn15％,Cu84％；所述Cu-Zn合金中各成分重量占比为：Cu75％,Zn25％；所述Cu-Sn合金中各成分重量占比为：Cu85％,Sn15％。
4.一种高寿命大理石刀头的制作方法，其特征在于，步骤如下：
1)按重量比将胎体粉末85-98％、金刚石2-15％原料均匀混合在一起，得到胎体和金刚石的混合料；胎体粉末配方组分由如下重量百分比组成：Cu-Sn-Si合金15-25％；Cu-Zn合金10-20％；Ni10-20％；Cu-Sn合金35-65％。
2)将混合料送入冷压机中压成刀头坯体；
3)将坯体装入石墨模具中进行烧结，制得高寿命大理石金刚石刀头。