The present invention relates to a special fertilizer for granular rice made from sandy raw materials and its manufacturing method and application. Calcium magnesium phosphate fertilizer, ammonium chloride and granulator with a weight ratio of 30 70:30 70:1 10 are mixed and added to the granulator for granulation. The granular material after granulation is then transferred to the dryer for drying, and the granular material after drying is then transferred to the cooling screen. Cooling screening in extension machine is available. Compared with the prior art, the present invention makes it easy to granulate by putting calcium magnesium phosphate fertilizer together with ammonium chloride and adding a little granulator, solves the nutritional requirement of rice, replaces and reduces the amount of other fertilizers.
【技术实现步骤摘要】
一种沙性原料制颗粒水稻专用肥及其制造方法和应用
本专利技术涉及肥料生产
，具体涉及一种沙性原料制颗粒水稻专用肥及其制造方法和应用。
技术介绍
水稻是中国第一大粮食作物，其播种面积约占粮食作物总面积的27％，稻谷产量占中国谷物总产40％以上。由于过量或不合理的施用化肥、微量元素的施用，导致土壤中营养比例失调，不能充分满足水稻生长所需的营养。中国专利CN103011986A公开了一种复方钙镁磷肥的生产方法，是在现有钙镁磷肥的基础上添加似斑状二长花岗岩或者麦饭石，腐植酸钠或腐植酸、尿素、聚丙烯酸钠、聚天门冬氨酸、硝酸稀土等制成。该方法虽说营养全，但由于各种有机原料及水不溶原料添加过多，成本高，肥料短期难以见效，适合做基肥，与农民希望短时见效的用肥习惯不一致。还有就是本方法未介绍具体造粒流程，不是任何粉末原料都能制成颗粒状，钙镁磷肥特别不易成粒。中国专利CN102557802B公开了一种水稻专用肥及其制备方法，所述专用肥是以尿素为核，以热法磷肥与钾肥和磷铵的混合物为包裹层的包裹型复合肥料，该肥料无机养分高，总养分可达到30％，不失为一种好的肥料，但由于易溶肥料尿素被...
【技术保护点】
1.一种沙性原料制颗粒水稻专用肥的制备方法，其特征在于，将重量比为30‑70：30‑70：1‑10的钙镁磷肥、氯化铵及造粒剂混合，加入造粒机中造粒，造粒后的颗粒物料再转入烘干机中烘干，烘干后的颗粒物料再转入冷却筛分机中冷却筛分，即得。
【技术特征摘要】
1.一种沙性原料制颗粒水稻专用肥的制备方法，其特征在于，将重量比为30-70：30-70：1-10的钙镁磷肥、氯化铵及造粒剂混合，加入造粒机中造粒，造粒后的颗粒物料再转入烘干机中烘干，烘干后的颗粒物料再转入冷却筛分机中冷却筛分，即得。2.根据权利要求1所述的一种沙性原料制颗粒水稻专用肥的制备方法，其特征在于，所述钙镁磷肥、氯化铵与造粒剂的重量比为40-66：32-60：2-10。3.根据权利要求1所述的一种沙性原料制颗粒水稻专用肥的制备方法，其特征在于，所述的造粒剂为膨润土、凹凸棒土、高岭土或粘土的一种或几种。4.根据权利要求1所述的一种沙性原料制颗粒水稻专用肥的制备方法，其特征在于，所述的造粒机为转鼓造粒机、圆盘造粒机或双轴造粒机。5.根据权利要求1所述的一种沙性原...
【专利技术属性】
技术研发人员：杨焕银，何耀，陈明良，李接励，袁宸，葛建国，廖红蕖，梁济，
申请(专利权)人：上海化工研究院有限公司，
类型：发明
国别省市：上海,31