一种干熄焦炉牛腿内衬制造技术

技术编号:21461025 阅读:65 留言:0更新日期:2019-06-26 07:55
本实用新型专利技术提供一种干熄焦炉牛腿内衬,在内衬损坏部位的牛腿耐火砖表面进行错列分布钻孔,钻孔内埋设耐热膨胀螺栓,耐热膨胀螺栓上焊接不同长度的耐热抓钉,设有耐热抓钉部位的耐火砖外面浇筑耐磨浇注料。本实用新型专利技术可避免牛腿及上部内环墙耐火砖全部拆除重砌,缩短检修工期,降低维修成本,有效提高牛腿内衬粘结强度,避免出现倒塌现象,延长牛腿的使用寿命。

A Kind of Bracket Lining for Dry Quenching Coke Oven

The utility model provides a bracket lining of a dry quenching coke oven. The bracket refractory brick surface of the damaged part of the bracket lining is drilled in staggered rows, heat-resisting expansion bolts are embedded in the drilling hole, heat-resisting screw of different lengths are welded on the heat-resisting expansion bolts, and wear-resisting castables are poured outside the refractory brick with heat-resisting screw parts. The utility model can avoid all demolition and rebuilding of the bracket and the refractory brick of the upper inner ring wall, shorten the overhaul period, reduce the maintenance cost, effectively improve the bonding strength of the bracket lining, avoid collapse and prolong the service life of the bracket.

【技术实现步骤摘要】
一种干熄焦炉牛腿内衬
本技术属于炼焦设备领域,尤其涉及一种干熄焦炉牛腿内衬。
技术介绍
目前,国内现有干熄焦炉牛腿均由耐火砖砌筑而成,这样的砌筑结构,整体性差,高温状态下“牛腿”受到内环墙体积膨胀产生的剪切应力作用,应力集中在前两排砖上,“牛腿”易断裂、脱落。在砖砌过程中,耐火泥的选用要求较高,在砌筑中火泥硬化强度较低,无法完全粘结,由于粘结抗折强度低,容易产生砖与砖之间及相邻两层砖层之间滑动,无法保证灰缝设计要求,烘炉膨胀均匀性改变后,产生的应力无法消除,斜道砖与顶部形成挤压,造成薄弱部分砖体受损断裂,影响牛腿使用寿命,制约干熄率的提高。
技术实现思路
本技术旨在提供一种可避免牛腿进一步损坏,提高牛腿使用寿命,降低维修成本的干熄焦炉牛腿内衬。为此,本技术所采取的技术解决方案为:一种干熄焦炉牛腿内衬,对于牛腿内衬损坏部位,由耐火砖砌筑结构改为耐火砖作骨架支撑、浇注料与锚固件作为表面保护的浇筑结构;在内衬损坏部位的牛腿耐火砖表面进行错列分布钻孔,钻孔内埋设耐热膨胀螺栓,耐热膨胀螺栓上焊接耐热抓钉,设有耐热抓钉部位的耐火砖外面浇筑耐磨浇注料。本技术的有益效果为:本技术可避免牛腿及上部内环墙耐本文档来自技高网...

【技术保护点】
1.一种干熄焦炉牛腿内衬,其特征在于,对于牛腿内衬损坏部位,由耐火砖砌筑结构改为耐火砖作骨架支撑、浇注料与锚固件作为表面保护的浇筑结构;在内衬损坏部位的牛腿耐火砖表面进行错列分布钻孔,钻孔内埋设耐热膨胀螺栓,耐热膨胀螺栓上焊接耐热抓钉,设有耐热抓钉部位的耐火砖外面浇筑耐磨浇注料。

【技术特征摘要】
1.一种干熄焦炉牛腿内衬,其特征在于,对于牛腿内衬损坏部位,由耐火砖砌筑结构改为耐火砖作骨架支撑、浇注料与锚固件作为表面保护的浇筑结构;在内...

【专利技术属性】
技术研发人员:徐吉国刘占博赵恒波马银华尹德刚魏春满
申请(专利权)人:鞍钢股份有限公司
类型:新型
国别省市:辽宁,21