The invention discloses an ionic gel with temperature and light responsiveness, and a preparation method and application thereof, belonging to the field of ionic gels. The ionic gels were prepared by mixing the butyl acrylate, azobenzene methacrylate, two methacrylic acid glycol ester, initiator and ionic liquid evenly. After deoxygenation, the temperature was heated to 60~80 degrees centigrade, and the reaction product was 10 ~ 24h under the protection of protective gas. The reaction product was soaked in ionic liquid to remove the unreactive monomer and the ionic gels were obtained. The ionic gels prepared by this application show temperature and light responsiveness, and can achieve light responsiveness.
【技术实现步骤摘要】
一种具有温度和光响应性的离子凝胶及其制备方法和应用
本申请属于离子凝胶
，更具体地说，涉及一种具有温度和光响应性的离子凝胶及其制备方法和应用。
技术介绍
离子凝胶是一类新型功能杂化材料，它是将离子液体分散于三维网络结构的连续聚合物固态相中，具有软物质良好的机械强度并保留了离子液体的优点。响应性离子凝胶具有环境响应性，即它可以随环境条件如电、温度、溶剂等的改变而呈现不同的形态。例如聚苯乙烯-聚甲基丙烯酸甲酯-聚苯乙烯三嵌段共聚物离子凝胶在电激励下能够产生明显的尺寸与形状变化，而在机械振动下能够产生相应的电激励信号；又如化学交联的聚N-异丙基丙烯酰胺(PNIPAm)离子凝胶在离子液体中具有高临界溶液温度相分离行为，呈现出在低温下收缩和高温下溶胀的现象；又如化学交联的聚丙烯酸卞酯或聚甲基丙烯酸丁酯在离子液体中具有低临界溶液温度相分离的行为，呈现出在低温下溶胀和高温下收缩的现象。致动器的工作原理是将其他能量转换为机械能，由于具有环境响应性，因此离子凝胶可以作为致动器使用。现有的离子凝胶致动器有两类，一类是电致动器，另一类是温度致动器。在光电材料、功能膜材料和生物传感...
【技术保护点】
1.一种具有温度和光响应的离子凝胶的制备方法，其特征在于，将丙烯酸正丁酯、甲基丙烯酸偶氮苯酯、二甲基丙烯酸乙二醇酯、引发剂和离子液体混合搅拌均匀，除氧后升温至40～80℃，在保护气体保护下反应10～48h，将反应产物浸泡在离子液体中以去除未反应的单体，得到离子凝胶。
【技术特征摘要】
1.一种具有温度和光响应的离子凝胶的制备方法，其特征在于，将丙烯酸正丁酯、甲基丙烯酸偶氮苯酯、二甲基丙烯酸乙二醇酯、引发剂和离子液体混合搅拌均匀，除氧后升温至40～80℃，在保护气体保护下反应10～48h，将反应产物浸泡在离子液体中以去除未反应的单体，得到离子凝胶。2.根据权利要求1所述的具有温度和光响应的离子凝胶的制备方法，其特征在于，丙烯酸正丁酯和甲基丙烯酸偶氮苯酯的总量占离子液体的质量分数为5％～40％，丙烯酸正丁酯和甲基丙烯酸偶氮苯酯的物质的量之比为60:40～99:1。3.根据权利要求1所述的具有温度和光响应的离子凝胶的制备方法，其特征在于，二甲基丙烯酸乙二醇酯的用量为丙烯酸正丁酯和甲基丙烯酸偶氮苯酯二者总物质的量的0.5～4％，优选1％。4.根据权利要求1所述的具有温度和光响应的离子凝胶的制备方法，其特征在于，引发剂的用量为丙烯酸正丁酯和甲基丙烯酸偶氮苯酯二者总物质的量的0.5～4％，优选1％。5.根据权利要求1或4所述的具有温度和光响应的离子...