The invention provides a preparation method of a graft copolymer, a graft copolymer and a thermoplastic resin mold product. The preparation methods of the graft copolymer include: 1) adding conjugated diene monomers and polymerizing them to prepare conjugated diene polymers; 2) adding and polymerizing the conjugated diene polymers, aromatic vinyl monomers and vinyl cyano monomers to prepare the graft copolymers, in which an emulsifier with APHA color value below 50 and critical micelle concentration between 1 g/l and 50 g/l is added; It shows excellent polymerization stability, dyeing performance, light resistance and surface clarity.
【技术实现步骤摘要】
【国外来华专利技术】接枝共聚物的制备方法、接枝共聚物和热塑性树脂模制品
相关申请的交叉引用本申请要求于2017年09月25日提交的韩国专利申请No.10-2017-0123356、No.10-2017-0123357、No.10-2017-0123358和No.10-2017-0123359，以及于2018年09月19日提交的韩国专利申请No.10-2018-0112003的优先权和权益，这些申请的公开内容通过引用全部并入本说明书中。
本专利技术涉及一种接枝共聚物的制备方法、接枝共聚物和热塑性树脂模制品，更具体地，涉及一种接枝共聚物的制备方法、接枝共聚物和热塑性树脂模制品，其表现出优异的聚合稳定性、着色性能、耐光性和表面清晰度(surfaceclarity)。
技术介绍
丙烯腈-丁二烯-苯乙烯(ABS)接枝共聚物由于丙烯腈的刚性和耐化学性以及丁二烯聚合物和苯乙烯的加工性能、机械强度和精制外观而广泛用于汽车、电气/电子产品、办公设备等的部件中。ABS接枝共聚物的表面光泽度和清晰度是决定模制品质量的重要因素。此外，由于ABS接枝共聚物在高温(200℃至250℃)下经过连续工艺，因此...
【技术保护点】
1.一种接枝共聚物的制备方法，包括：1)添加共轭二烯类单体并进行聚合以制备共轭二烯类聚合物；以及2)添加所述共轭二烯类聚合物、芳香族乙烯基单体和乙烯基氰基单体并进行聚合以制备接枝共聚物，其中，添加具有50以下的APHA色值和1g/l至50g/l的临界胶束浓度的乳化剂。
【技术特征摘要】
【国外来华专利技术】2017.09.25 KR 10-2017-0123356;2017.09.25 KR 10-2011.一种接枝共聚物的制备方法，包括：1)添加共轭二烯类单体并进行聚合以制备共轭二烯类聚合物；以及2)添加所述共轭二烯类聚合物、芳香族乙烯基单体和乙烯基氰基单体并进行聚合以制备接枝共聚物，其中，添加具有50以下的APHA色值和1g/l至50g/l的临界胶束浓度的乳化剂。2.根据权利要求1所述的制备方法，其中，所述乳化剂是具有50以下的APHA色值的松香酸碱金属盐。3.根据权利要求1所述的制备方法，其中，所述乳化剂是具有50以下的APHA色值的松香酸钾。4.根据权利要求1所述的制备方法，其中，所述乳化剂在步骤1)中添加。5.根据权利要求1所述的制备方法，其中，相对于100重量份的所述共轭二烯类单体，所述乳化剂在步骤1)中以0.1重量份至5重量份的量添加。6.根据权利要求1所述的制备方法，其中，所述乳化剂的全部在步骤1)中聚合开始之前添加。7.根据权利要求1所述的制备方法，其中，所述乳化剂在步骤1)中当聚合转化率在30％至40％和60％至70％的区间中时部分地添加。8.根据权利要求1所述的制备...
【专利技术属性】
技术研发人员：金由彬，金英玟，李镇衡，韩受静，郑荣焕，石宰旼，许宰源，
申请(专利权)人：株式会社LG化学，
类型：发明
国别省市：韩国,KR