本发明专利技术公开了一种以废旧水泥为原料制备锂电池负极材料的方法。制备过程为：选取建筑物废旧水泥、公路废旧水泥中的一种，砸碎，清洗干净后烘干，研磨成粉末，之后，将其置于坩埚中，在马弗炉内于400～900℃下煅烧1‑5个小时，即得到锂电池负极材料。实验证明，本发明专利技术所制备的材料具有一定的放电比容量，较好的循环稳定性，可作为锂电池负极材料使用。同时，本发明专利技术实现了对建筑垃圾的回收再利用。

A Method of Preparing Lithium Battery Anode Material Using Waste Cement as Raw Material

The invention discloses a method for preparing lithium battery negative electrode material with waste cement as raw material. The preparation process is as follows: one of the waste cement of buildings and highway is selected, crushed, cleaned, dried, ground into powder, then placed in crucible, calcined in muffle furnace at 400-900 C for 1 5 hours, then lithium battery anode material is obtained. The experiment proves that the material prepared by the invention has certain discharge specific capacity and good cycle stability, and can be used as negative electrode material of lithium battery. At the same time, the invention realizes the recovery and reuse of construction waste.

【技术实现步骤摘要】
一种以废旧水泥为原料制备锂电池负极材料的方法
本专利技术涉及一种以废旧水泥为原料制备锂电池负极材料的方法，属于能源材料

技术介绍
锂离子电池，也称为锂电池，具有电压高、循环寿命长、安全性能好、充电迅速等优点，在手机、笔记本电脑、数码相机等电子设备中得到了广泛应用。在锂离子电池中，负极材料的性能是影响电池容量和使用寿命的重要因素之一。目前锂离子电池中常以碳材料石墨作为负极材料使用，但最近研究发现石墨的电位与金属锂的电位很接近，在充电时容易产生锂枝晶，在一些特殊情况下，锂枝晶可能会刺破隔膜引起短路，导致安全事故的发生。最近人们发现金属氧化物也可作为锂离子电池负极材料使用，但金属氧化物存在导电性差、制作成本高等缺点。因此研发新型锂离子电池负极材料仍是锂电池研究领域中的重要研究课题之一。社会的发展使建筑材料的需求量不断增大，与此同时，建筑垃圾的产出也是触目惊心，建筑垃圾的循环利用以及相应的回收处理就成为人们不得不面对的问题了。在建筑垃圾中，废旧水泥占据很大比例，因此，废旧水泥的回收再利用就显得尤为重要。
技术实现思路
本专利技术的目的在于提供一种以废旧水泥为原料制备锂电池负极材料的方法本文档来自技高网...

【技术保护点】
1. 一种以废旧水泥为原料制备锂电池负极材料的方法，其特征在于包括以下步骤：原料的准备取建筑物废旧水泥、公路废旧水泥中的一种为原料，备用；样品的制备取一定量上述废旧水泥块，砸碎，清洗干净，烘干，研磨成粉末状，放在坩埚中，置于马弗炉内于400～900℃下煅烧1‑5小时，即得到锂电池负极材料。

【技术特征摘要】
1.一种以废旧水泥为原料制备锂电池负极材料的方法，其特征在于包括以下步骤：原料的准备取建筑物废旧水泥、公路废旧水泥中的一种为原料，备用；样品的制...