The invention discloses a preparation method of graphene/graphene oxide coated with nickel metal layer, which includes: pretreatment of graphene/graphene oxide surface with graphene/graphene oxide as carrier, filtration, separation and drying, reaction of graphene/graphene oxide in electroless nickel plating solution, and then obtaining metal through filtration, separation and drying steps. Nickel coated graphene/graphene oxide powder. By electroless plating technology, the complete coated nickel layer can be formed on the surface of graphene/graphene oxide. The thickness of the nickel layer can be controlled, and the combination with graphene/graphene oxide is good. The coated powder has both characteristics, and improves the wettability of graphene and metal and the compatibility in oil (grease). By improving the chemical stability and dispersion of graphene/graphene oxide in lubricating oil (grease), the performance of graphene/graphene oxide additive lubricating oil (grease) was improved.
【技术实现步骤摘要】
一种金属镍层包覆石墨烯/氧化石墨烯的制备方法
本专利技术涉及石墨烯/氧化石墨烯表面改性工艺
，具体涉及一种金属镍层包覆石墨烯/氧化石墨烯的制备方法。
技术介绍
在机械工程领域，摩擦是普遍存在的现象，不仅消耗能量，而且造成资源的大量浪费。我国每年因摩擦磨损造成的损失占到国民总产值的15％以上。添加润滑油的目的就是控制摩擦减少磨损，通过减少摩擦功的损失实现节能;另外使摩擦发生在填料(或称添加剂)层，则可有效减少磨损，防止材料的损失以保证零件的正常工作。因此润滑油添加剂对提高材料耐磨抗磨性能至关重要。目前，由于传统润滑油的润滑能力有限以及传统润滑油中添加的含硫、磷、氯等元素的添加剂对环境造成严重污染，因此，新型润滑油添加剂的研究受到国内外众多学者的广泛关注。石墨烯（GrapHene）是一种由碳原子以sp²杂化轨道组成六角型呈蜂巢晶格的二维碳纳米材料，具有优异的光学、电学、力学特性，在材料学、微纳加工、能源、生物医学和药物传递等方面具有重要的应用前景，被认为是一种未来革命性的材料。石墨烯作为新兴的材料，在润滑油(脂)中的应用中以润滑和防锈两个方面有所突破。由于石墨烯...
【技术保护点】
1.一种金属镍层包覆石墨烯/氧化石墨烯的制备方法，其特征在于，包括：以石墨烯/氧化石墨烯作为载体，将石墨烯/氧化石墨烯表面进行预镀处理后，经过过滤、分离、干燥后，将所述石墨烯/氧化石墨烯放入化学镀镍液中反应，再经过滤、分离、干燥的步骤获得金属镍层包覆的石墨烯/氧化石墨烯粉末。
【技术特征摘要】
1.一种金属镍层包覆石墨烯/氧化石墨烯的制备方法，其特征在于，包括：以石墨烯/氧化石墨烯作为载体，将石墨烯/氧化石墨烯表面进行预镀处理后，经过过滤、分离、干燥后，将所述石墨烯/氧化石墨烯放入化学镀镍液中反应，再经过滤、分离、干燥的步骤获得金属镍层包覆的石墨烯/氧化石墨烯粉末。2.根据权利要求1所述的方法，其特征在于，所述载体为单层石墨烯、多层石墨烯、掺杂石墨烯、氧化石墨烯或缺陷石墨烯。3.根据权利要求1所述的方法，其特征在于，所述化学镀镍液由主盐、还原剂、络合剂、pH缓冲剂和稳定剂构成。4.根据权利要求1所述的方法，其特征在于，所述将所述石墨...