The invention relates to an environmental protection building adhesive and a preparation method thereof. The environmental protection building adhesive is prepared by using lignin gum, xanthan gum, polyvinyl alcohol, epoxy resin, hydroxyl cellulose, carbon fiber particles, surfactant and silane coupling agent as raw materials and appropriate weight ratio, and has strong adhesion, high compressive and tensile strength. The film forming and curing time is short, the use is convenient, the construction efficiency is high, and the building glue is non-toxic and tasteless, and belongs to the green environmental protection product. The data show that the peeling strength of the high strength building glue is over 14 Mpa and the tensile shear strength is over 20 Mpa.
【技术实现步骤摘要】
一种环保建筑胶及其制备方法
本专利技术属于建筑胶
，具体涉及一种环保建筑胶及其制备方法。
技术介绍
随着社会的发展和生活水平的提高，建筑、装潢行业对建筑胶粘剂的需求日渐增加。目前使用的传统建筑胶粘剂的胶粘强度、防水等指标不能满足需求，并且大部分含有醛类、有机溶剂等大量有害物质，对居住环境和人体健康造成极大的影响。随着人们健康意识的增强，室内的装修和环境越来越受到重视，传统的建筑胶粘剂逐渐被淘汰，具有高性能、环保的建筑胶粘剂越来越受关注，具有极大的市场需求。
技术实现思路
为了解决现有技术存在的上述问题，本专利技术提供了一种环保建筑胶及其制备方法。所述环保建筑胶，粘合力强，抗压和抗拉强度高，成膜和固化时间短，使用方便，施工效率高，并且所述建筑胶无毒、无味，属于绿色环保产品。本专利技术所采用的技术方案为：一种环保建筑胶，原料组分包括：木质素胶和黄原胶的混合物，30-50重量份；聚乙烯醇，5-15重量份；环氧树脂，10-20重量份；羟基纤维素，1-5重量份；碳纤维颗粒，0.8-2重量份；表面活性剂，1.2-2.4重量份；硅烷偶联剂，1.2-2.4重量份；水，100-3...
【技术保护点】
1.一种环保建筑胶，其特征在于，原料组分包括：木质素胶和黄原胶的混合物，30‑50重量份；聚乙烯醇，5‑15重量份；环氧树脂，10‑20重量份；羟基纤维素，1‑5重量份；碳纤维颗粒，0.8‑2重量份；表面活性剂，1.2‑2.4重量份；硅烷偶联剂，1.2‑2.4重量份；水，100‑300重量份。
【技术特征摘要】
1.一种环保建筑胶，其特征在于，原料组分包括：木质素胶和黄原胶的混合物，30-50重量份；聚乙烯醇，5-15重量份；环氧树脂，10-20重量份；羟基纤维素，1-5重量份；碳纤维颗粒，0.8-2重量份；表面活性剂，1.2-2.4重量份；硅烷偶联剂，1.2-2.4重量份；水，100-300重量份。2.根据权利要求1所述的环保建筑胶，其特征在于，原料组分包括：木质素胶和黄原胶的混合物，40重量份；聚乙烯醇，10重量份；环氧树脂，15重量份；羟基纤维素，3重量份；碳纤维颗粒，1.4重量份；表面活性剂，1.8重量份；硅烷偶联剂，1.8重量份；水，200重量份。3.根据权利要求1所述的环保建筑胶，其特征在于，所述木质素胶和黄原胶的质量比为1-4:1-4。4.根据权利要求1所述的环保建筑胶，其特征在于，所述羟基纤维素包括羟甲基纤维素、羟乙基纤维素、羟丙基甲基纤维素中的一种或几种的混合物。5.根据权利要求4所述的环保建筑胶，其特征在于，所述羟基纤维素为羟甲基纤维素、羟乙基纤维素、羟丙基甲基纤维素...
【专利技术属性】
技术研发人员：林辉，
申请(专利权)人：广州市长迅环保科技有限公司，
类型：发明
国别省市：广东,44