A novel superhydrophobic functional coating and its preparation method include the following steps: 1) dissolving epoxy resin in solvent, then adding glass beads to mix into liquid A; 2) dissolving nanohydrophobic silicon dioxide in solvent, stirring and ultrasonic to obtain liquid B; 3) spraying liquid A on the surface of the substrate at room temperature for solvent evaporation; and then slowly immersing the matrix into liquid B and stationary. The matrix can be solidified at room temperature after volatilization of solvent. The prepared superhydrophobic coating has good adhesion and transparency, and plays a certain role in promoting the application of superhydrophobic materials in water droplet collection and micro-liquid transportation.
【技术实现步骤摘要】
一种新型超疏水功能涂层及其制备方法
本专利技术涉及一种新型超疏水功能涂层及其制备方法,在实现超疏水性的同时也展现了良好粘附性和较好的透明性。
技术介绍
超疏水性固体表面是指表面对水的接触角在150°以上,前进接触角和后退接触角的差<10°的固体表面。降低材料的表面自由能和增加材料表面的微观粗糙度是提高材料表面疏水性的重要途径。超疏水表面可以分为两类:一是低粘附性超疏水表面,水滴浸润面积小,如荷叶表面;二是高粘附性超疏水表面,水滴浸润面积大,如玫瑰花表面。粘附性是超疏水表面的一个重要特性,目前超疏水表面局限于超疏水性而低粘附性。
技术实现思路
本专利技术的专利技术目的是提供了一种新型超疏水功能涂层,不仅能在材料表面实现超疏水功能,同时还具有一定的粘附性和较好的透明性,同时提供其制备方法是本专利技术的又一专利技术目的。为实现上述专利技术目的,本专利技术采取的技术方案为:一种新型超疏水功能涂层的制备方法,包括以下步骤:1)将环氧树脂溶于溶剂中,再加入玻璃微珠混合得A液;2)将纳米疏水二氧化硅溶于溶剂中,经搅拌、超声得B液;3)将A液喷涂于基体表面上,置于室温下待表面溶剂挥发 ...
【技术保护点】
1.一种新型超疏水功能涂层的制备方法,其特征在于,包括以下步骤:1)将环氧树脂溶于溶剂中,再加入玻璃微珠混合得A液;2)将纳米疏水二氧化硅溶于溶剂中,经搅拌、超声得B液;3)将A液喷涂于基体表面上,置于室温下待表面溶剂挥发;之后将上述基体缓慢浸入B液并静置;取出基体待溶剂挥发后在室温下固化即可;所述溶剂为无水乙醇、丙酮、甲苯、四氢呋喃和乙酸乙酯中的一种。
【技术特征摘要】
1.一种新型超疏水功能涂层的制备方法,其特征在于,包括以下步骤:1)将环氧树脂溶于溶剂中,再加入玻璃微珠混合得A液;2)将纳米疏水二氧化硅溶于溶剂中,经搅拌、超声得B液;3)将A液喷涂于基体表面上,置于室温下待表面溶剂挥发;之后将上述基体缓慢浸入B液并静置;取出基体待溶剂挥发后在室温下固化即可;所述溶剂为无水乙醇、丙酮、甲苯、四氢呋喃和乙酸乙酯中的一种。2.如权利要求1所述的新型超疏水功能涂层的制备方法,其特征在于,步骤1)中,A液中,环氧树脂、玻璃微珠的用量分别为溶剂质量的2%~3%和2%~5%;混合时采用搅拌的方式,搅拌速度为200r/min~300r/min,搅拌时间为1h~2h。3.如权利要求1所述的新型超疏水的功能涂层的制备方法,其特征在于,步骤2)中,B液中,疏水二氧化硅的用量为溶剂质量的2%~4%;搅拌速度为200r/min~300r/min,搅拌时间为30min~60...