The invention discloses a medical porous fiber membrane and a preparation method thereof, using gelatin, konjac glucomannan and sodium hyaluronate as main raw materials, glacial acetic acid as solvent, adding nano-hydroxyapatite to increase the strength and toughness of the porous membrane, and preparing a sodium hyaluronate/gelatin/konjac glucomannan/nano-hydroxyapatite porous fiber membrane. The method is simple and convenient. The prepared medical porous fibrous membrane has good mechanical properties and good biocompatibility. Physically cross-linked porous fibrous membrane materials have great potential in artificial skin, skin dressing, drug loading, cartilage repair, cancellous bone micro-defect and so on.
【技术实现步骤摘要】
一种医用多孔纤维膜及其制备方法
本专利技术涉及一种医用多孔纤维膜材料及其制备方法，属于生物医学材料
技术介绍
人类的皮肤来源有限，而异体皮肤移植会发生免疫排斥反应，因此人们一直在寻找和研究可以治疗皮肤灼伤的材料，并且它们具有某种皮肤功能，人们把这类材料通常称为人造皮肤原料。它是从用于治疗皮肤灼伤的早期医用敷料开发而来的。医用纤维膜因孔隙率高、比表面积大、吸附性和过滤性强等优点，广泛应用于生物医用功能材料，可在生物体表面外敷可促进伤口愈合、也可以用于载药、软骨修复、松质骨微缺损等。医用多孔纤维膜材料作为伤口敷料，可以有效地免交叉感染，治疗时间短，减少病苦，减轻工作量。随着负压封闭引流技术的不断发展，引流创面敷料材料的开发也日益得到关注，而其中敷料起到保护创面、防止体液和蛋白质流失，并对增殖细胞提供支撑。但是现有的医用敷料普遍存在机械强度不足和生物相容性较差，并且制作工艺繁琐，抗感染性差等问题，阻碍了其进一步使用。
技术实现思路
本专利技术提供一种医用多孔纤维膜，其特征在于，以透明质酸钠、明胶、魔芋葡甘聚糖、纳米羟基磷灰石为原料，通过静电纺丝制得。本专利技术还提...
【技术保护点】
1.一种医用多孔纤维膜，其特征在于，以透明质酸钠、明胶/、魔芋葡甘聚糖、纳米羟基磷灰石为原料，通过静电纺丝制得。
【技术特征摘要】
1.一种医用多孔纤维膜，其特征在于，以透明质酸钠、明胶/、魔芋葡甘聚糖、纳米羟基磷灰石为原料，通过静电纺丝制得。2.权利要求1所述医用多孔纤维膜的制备方法，其特征在于，具体步骤如下：（1）在磁力搅拌条件下，将明胶与冰乙酸混合，明胶完全溶解且液体内部肉眼观察不到气泡，得到混合物A；（2）在磁力搅拌条件下，在步骤（1）混合物A中加入魔芋葡甘聚糖，得到混合物B；（3）在磁力搅拌条件下，将透明质酸钠放入蒸馏水中混合均匀，得到混合物C；（4）在磁力搅拌条件下，在步骤（2）混合物B中加入步骤（3）混合物C，得到混合物D；（5）在磁力搅拌条件下，在步骤（4）混合物D中加入纳米羟基磷灰石，得到混合物E；（6）在磁力搅拌条件下，将步骤（5）混合物E中加入丙三醇，得到混合物F；（7）将步骤（6）混合物F进行静电纺丝，制得医用透明质酸钠/明胶/魔芋葡甘聚糖/纳米羟基磷灰石多孔纤维膜。3.根据权利要求2所述医用多孔纤维膜的制备方法，...
【专利技术属性】
技术研发人员：冷崇燕，竹泳俊，陈庆华，支燕，汪虹，刘金坤，严继康，颜廷亭，陈希亮，
申请(专利权)人：昆明理工大学，
类型：发明
国别省市：云南,53
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。