The invention provides a workpiece spraying method, whose process is as follows: 1. cleaning the workpiece surface before spraying; 2. uniformly spraying paint on the workpiece surface; 3. low temperature baking intervention heat; 4. high temperature baking intervention finalization; 5. low temperature baking intervention finalization; 6. high temperature baking finalization. This method can combine coating with workpiece better by four steps: low temperature baking intervention heat, high temperature baking intervention stereotyping, low temperature baking intervention stereotyping and high temperature baking stereotyping, improve the utilization rate of baking equipment, reduce the baking cost, and has the advantages of simple structure, convenient use and high efficiency.
【技术实现步骤摘要】
一种工件喷涂方法
本专利技术属于机械加工领域，尤其是涉及一种工件喷涂方法。
技术介绍
喷涂工艺是工件及表面修复、防护和强化的新技术，使其具备耐腐蚀、耐磨损、耐高温、抗氧化等特殊性能，达到提高产品质量，延长使用寿命。现有技术中喷涂时，涂料和工件不易定型，且喷涂效率低下，严重影响效率。
技术实现思路
有鉴于此，本专利技术旨在提出一种工件喷涂方法，提高喷涂效率。为达到上述目的，本专利技术的技术方案是这样实现的：一种工件喷涂方法，其过程如下：1、对工件表面进行喷涂前清洁；2、将涂料均匀喷涂在工件表面；3、低温烘干预热：将工件置于40℃-50℃的温度条件下烘烤20秒至30秒；4、高温烘干预定型：将工件置于60℃-80℃的温度条件下烘烤15秒至20秒；5、低温烘干预定型：将工件置于40℃-50℃的温度条件下烘烤10秒至15秒；6、高温烘干定型：将工件置于70℃-90℃的温度条件下烘烤10秒至15秒。进一步的，喷涂时的涂层厚度为5-8mm。进一步的，所述喷涂涂料包括双酚A型环氧树脂、改性胺类固化剂、三聚氰胺树脂、低碳醇、偏苯三甲酸酐、甲乙酮、酚醛树脂和阻燃剂。进一步的，所述喷涂涂料...
【技术保护点】
1.一种工件喷涂方法，其特征在于，其过程如下：1)对工件表面进行喷涂前清洁；2)将涂料均匀喷涂在工件表面；3)低温烘干预热：将工件置于40℃‑50℃的温度条件下烘烤20秒至30秒；4)高温烘干预定型：将工件置于60℃‑80℃的温度条件下烘烤15秒至20秒；5)低温烘干预定型：将工件置于40℃‑50℃的温度条件下烘烤10秒至15秒；6)高温烘干定型：将工件置于70℃‑90℃的温度条件下烘烤10秒至15秒。
【技术特征摘要】
1.一种工件喷涂方法，其特征在于，其过程如下：1)对工件表面进行喷涂前清洁；2)将涂料均匀喷涂在工件表面；3)低温烘干预热：将工件置于40℃-50℃的温度条件下烘烤20秒至30秒；4)高温烘干预定型：将工件置于60℃-80℃的温度条件下烘烤15秒至20秒；5)低温烘干预定型：将工件置于40℃-50℃的温度条件下烘烤10秒至15秒；6)高温烘干定型：将工件置于70℃-90℃的温度条件下烘烤10秒至15秒。2.根据权利要求1所述的一种工件喷涂方法，其特征在于：喷涂时的涂层厚度为5-8mm。3.根据权利要求1所述的一种工件喷涂方法，其特征在于：所...