The invention provides an on-line production process and method for heating non-combustible cigarettes, in which the feeding process of cigarettes is carried out immediately after the loose moisture regaining process of cigarettes. In the loose moisture regaining process, the moisture content of the loose moisture regaining outlet is 14wt%16wt%, and the temperature of the loose moisture regaining hot air is above 60 ~C. The process can not only produce in batches without blocking the smoke gun, but also solve the problem of macula smoke, while keeping the amount of smoke from heating and non-burning cigarettes basically unchanged.
【技术实现步骤摘要】
加热不燃烧卷烟在线生产工艺及方法
本专利技术涉及烟草加工领域，具体涉及一种加热不燃烧卷烟在线生产工艺及方法。
技术介绍
公开该
技术介绍
部分的信息仅仅旨在增加对本专利技术的总体背景的理解，而不必然被视为承认或以任何形式暗示该信息构成已经成为本领域一般技术人员所公知的现有技术。加热不燃烧卷烟(heat-not-burncigarette)，通过外部热源对烟草物质进行加热，烟草物质中的雾化介质、香味成分和外加香通过加热产生类似于传统卷烟燃吸的烟雾，使消费者得到生理满足感。低温卷烟中的烟草物质只加热而不燃烧，且加热温度(250℃～350℃)远低于传统卷烟的燃烧温度(800℃-900℃)，因此，烟气有害成分和生物毒性大幅降低，同时，与传统卷烟阴燃不同，它在抽吸间歇时烟草物质处于非加热状态，因此侧流烟气和环境烟气也大幅度降低。实验室生产加热不燃烧卷烟的工艺流程往往包括依次进行烟片松散、烟片回潮、烟片密闭贮存、切丝、烘丝、烘后烟丝加香加料、烟丝密闭贮存、卷制包装的工序。此外，上述工艺以及常规的卷烟生产工艺中，参数情况为：卷烟的回潮烟片水分为15％～20％，生产线加料比例为2％～...
【技术保护点】
1.一种加热不燃烧卷烟的在线生产工艺，其烟片加料工序紧接在烟片松散回潮工序后进行，其中，松散回潮工序中，松散回潮出口水分为14wt％‑16wt％，松散回潮热风温度为60℃以上。
【技术特征摘要】
1.一种加热不燃烧卷烟的在线生产工艺，其烟片加料工序紧接在烟片松散回潮工序后进行，其中，松散回潮工序中，松散回潮出口水分为14wt％-16wt％，松散回潮热风温度为60℃以上。2.根据权利要求1所述的生产工艺，其特征在于，松散回潮工序中，松散回潮出口水分为14-15wt％；优选地，松散回潮工序中，松散回潮热风温度为63-65℃。3.根据权利要求1或2所述的生产工艺，其特征在于，烟片加料工序中，加料比例为不低于18wt％，优选为18-30wt％。4.根据权利要求1或2所述的生产工艺，其特征在于，烟片加料工序中，加料料液温度为不低于60℃，优选为60-65℃；优选地，烟片加料工序中，热风温度为不低于60℃，优选为63-65℃。5.根据权利要求1或2所述的生产工艺，其特征在于，烟片加料工序完成后烟片密闭贮存；优选地，烟片密闭贮存的时间不小于48小时。6.根据权利要求1或2所述的生产工艺，其特征在于，烟片密闭贮存后为切丝工序，烟片被切成烟丝。7.根据权利要求1或2所述的生产工艺，其特征在于，切丝工序后为烘丝工序；优选地，烘丝工序中采用滚筒烘丝；优选地，烘丝工序中，采用低强度干燥，其中，筒壁温度为115℃～130℃，热风温度90℃～110℃，烘丝...
【专利技术属性】
技术研发人员：吴克志，王京林，王钧，刘开俊，管仕栓，周仕禄，蒋光伟，刘仕民，李洪涛，王青海，刘晓倩，张莎莎，米强，刘杰，
申请(专利权)人：山东中烟工业有限责任公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。