The invention relates to a separator processing technology for office supplies, which includes: (1) putting kyanite into a ball mill for continuous milling for 2 hours; (2) putting kyanite powder, flame retardant modified vinyl chloride, seaweed powder and modified starch in the furnace device together in step (1) heating to 1200 (?) for 3 hours; (3) adding modified ceramic powder in step (2) heating to 1550 (?) After holding for 1 hour, the temperature is lowered to 860 C within 20 to 45 minutes, then heated to 1610 C with 150 C/h for 2 hours; (4) The materials in step (3) are fed into the forming machine to make different sizes of partitions, which can be cooled naturally. The finished product of the invention is firm, durable and flame retardant.
【技术实现步骤摘要】
一种办公用品的隔板加工工艺
本专利技术涉及一种隔板，具体涉及一种隔板加工工艺。
技术介绍
现有的隔板材料，材料性能一般，普遍存在原材料配比复杂，加工成本高等问题，不符合实际生产要求。
技术实现思路
专利技术目的：本专利技术的目的是为了克服现有技术中的不足，提供一种成品坚实耐用，阻燃的办公用品的隔板加工工艺。技术方案：为了解决上述技术问题，本专利技术所述的一种办公用品的隔板加工工艺，它包括以下步骤，（1）将蓝晶石放入球磨机中连续球磨2小时；（2）将步骤（1）中的蓝晶石粉、阻燃改性氯乙烯、海菜粉、变性淀粉一起放入熔炉装置，加热至1200℃，保温3小时；（3）再在步骤（2）中加入改性陶瓷粉，加热至1550℃，保温1小时，然后在20-45分钟内降温至860℃，再以150℃/h加热至1610℃，保温2小时；（4）将步骤（3）中的物料送入成型机，制成不同规格的隔板，自然冷却即可。有益效果：本专利技术与现有技术相比，其显著优点是：本专利技术通过严谨的加工步骤，使成品材料性能优异，整体坚实耐用，阻燃，符合实际生产要求。具体实施方式下面结合实施例对本专利技术作进一步的说明。本专利技术所述的一种办公用品的隔板加工工艺，它包括以下步骤，（1）将蓝晶石放入球磨机中连续球磨2小时；（2）将步骤（1）中的蓝晶石粉、阻燃改性氯乙烯、海菜粉、变性淀粉一起放入熔炉装置，加热至1200℃，保温3小时；（3）再在步骤（2）中加入改性陶瓷粉，加热至1550℃，保温1小时，然后在35分钟内降温至860℃，再以150℃/h加热至1610℃，保温2小时；（4）将步骤（3）中的物料送入成型机，制成不同规格的...
【技术保护点】
1.一种办公用品的隔板加工工艺，其特征在于：它包括以下步骤，（1）将蓝晶石放入球磨机中连续球磨2小时；（2）将步骤（1）中的蓝晶石粉、阻燃改性氯乙烯、海菜粉、变性淀粉一起放入熔炉装置，加热至1200℃，保温3小时；（3）再在步骤（2）中加入改性陶瓷粉，加热至1550℃，保温1小时，然后在20‑45分钟内降温至860℃，再以150℃/h加热至1610℃，保温2小时；（4）将步骤（3）中的物料送入成型机，制成不同规格的隔板，自然冷却即可。
【技术特征摘要】
1.一种办公用品的隔板加工工艺，其特征在于：它包括以下步骤，（1）将蓝晶石放入球磨机中连续球磨2小时；（2）将步骤（1）中的蓝晶石粉、阻燃改性氯乙烯、海菜粉、变性淀粉一起放入熔炉装置，加热至1200℃，保温3小时；（3...
【专利技术属性】
技术研发人员：王琴芬，
申请(专利权)人：江苏宇之源新能源科技有限公司，
类型：发明
国别省市：江苏,32