The invention relates to the technical field of building materials, in particular to a sound absorbing building material, which is made up of the following weight parts: 45 to 55 pieces of ceramsite, 15 to 20 parts of diatomite, 10 to 15 parts of calcium carbonate, 8 to 12 parts of silicon dioxide, 16 16 20 of acrylic acid, 15 parts of plant fiber 15; inorganic antibacterial agent; A sound absorbing building material of the invention is made of ceramic, diatomite, calcium carbonate, silica, acrylic emulsion, plant fiber, inorganic antibacterial agent, graphite powder, limestone and mixed stirring, and adopts ceramic and plant fiber ecological building materials, and the material is easy to obtain, which has good sound insulation and sound absorption effect, good heat preservation performance, no pollution and no poison, and is favorable for environmental protection. Protect and save energy.
【技术实现步骤摘要】
一种吸音建筑材料
本专利技术涉及建筑材料
，尤其是一种吸音建筑材料。
技术介绍
吸音材料吸声材料大多为疏松多孔的材料，如矿渣棉、毯子等，其吸声机理是声波深入材料的孔隙，且孔隙多为内部互相贯通的开口孔，受到空气分子摩擦和粘滞阻力，以及使细小纤维作机械振动，从而使声能转变为热能。这类多孔性吸声材料的吸声系数，一般从低频到高频逐渐增大，故对高频和中频的声音吸收效果较好。
技术实现思路
为了克服现有的建筑材料的不足，本专利技术提供了一种吸音建筑材料，将陶粒；硅藻土；碳酸钙；二氧化硅；丙烯酸乳液；植物纤维；无机抗菌剂；石墨粉；石灰石混合搅拌制成。本专利技术解决其技术问题所采用的技术方案是：一种吸音建筑材料，包括由以下重量份的组成制成：陶粒45-55份；硅藻土15-20份；碳酸钙10-15份；二氧化硅8-12份；丙烯酸乳液16-20份；植物纤维15-19份；无机抗菌剂1.5-2份；石墨粉2-5份；石灰石5-10份。进一步的，包括陶粒重量份为50份的时候效果最佳。进一步的，包括碳酸钙重量份为12份的时候效果最佳。进一步的，包括丙烯酸乳液重量份为18份的时候效果最佳。进一步的，包括植物纤维重量份为16份的时候效果最佳。本专利技术的有益效果是，本专利技术的一种吸音建筑材料，将陶粒；硅藻土；碳酸钙；二氧化硅；丙烯酸乳液；植物纤维；无机抗菌剂；石墨粉；石灰石混合搅拌制成，采用陶瓷和植物纤维生态建筑材料，原料易得，具有很好的隔音、吸音效果，保温性能良好，无污染、无毒害，有利于环境保护，而且节能。具体实施方式一种吸音建筑材料，包括由以下重量份的组成制成：陶粒45-55份；硅藻土1...
【技术保护点】
1.一种吸音建筑材料，其特征是，包括由以下重量份的组成制成：陶粒45‑55份；硅藻土15‑20份；碳酸钙10‑15份；二氧化硅8‑12份；丙烯酸乳液16‑20份；植物纤维15‑19份；无机抗菌剂1.5‑2份；石墨粉2‑5份；石灰石5‑10份。
【技术特征摘要】
1.一种吸音建筑材料，其特征是，包括由以下重量份的组成制成：陶粒45-55份；硅藻土15-20份；碳酸钙10-15份；二氧化硅8-12份；丙烯酸乳液16-20份；植物纤维15-19份；无机抗菌剂1.5-2份；石墨粉2-5份；石灰石5-10份。2.根据权利要求1所述的一种吸音建筑材料，其特征是，所述陶粒重量...
【专利技术属性】
技术研发人员：孙欣，
申请(专利权)人：常州市飞腾工业自动化技术有限公司，
类型：发明
国别省市：江苏,32