An impact resistant alloy plate is characterized by the following components: iron: 0.15%-0.25%, magnesium: 0.15%-1.80%, copper: 1.20%-2.00%, calcium: 0.40%-1.80%, titanium 0.2%-0.3%, zinc: 0.25%-0.75%, cadmium: <0.30%, zirconia: <0.12%, lead: <0.03%, iridium: <0.05%, selenium: <0.015%, platinum: <0.010%. The rest are aluminium and unavoidable impurities. By changing the traditional alloy material, adding cadmium, lead, titanium and other components, the invention improves the impact resistance of the sheet, increases the stability and coloring ability of the sheet, so as to further improve the comprehensive performance of the composite impact resistant alloy sheet.
【技术实现步骤摘要】
一种抗冲击合金板
本专利技术涉及金属板材
,具体涉及一种抗冲击合金板。
技术介绍
铝塑复合管是一种由中间纵焊铝管、内外层聚乙烯材料以及层与层之间热熔性共挤复合而成的新型管道。内外层聚乙烯易于成型、耐腐蚀性和耐低温性能好、低温抗冲击性能优异,管材级聚乙烯还具有高的长期耐压性能和耐环境应力开裂性能。中间层纵焊铝合金属管子具有金属的耐压强度和耐冲击能力,在铝塑管实际使用温度范围内,铝合金强度保持不变,为铝塑管的长期耐热性能提供了可靠的保障。由于铝塑复合管具有金属管坚固耐压和塑料管抗酸碱耐腐蚀的双重优点,被广泛应用于各种行业。在生产铝塑复合管时,先制备厚度约为0.2mm的铝抗冲击合金板,然后采用氩弧对接焊得到中间铝管。铝塑复合管对铝抗冲击合金板性能要求较低,但是要求铝合金的力学性能具有很好的稳定性,在现有技术中,经常采用AA1100铝合金制备铝塑复合管。AA1100铝合金为纯铝中添加少量铜元素形成,其典型成分为:0.05wt%~0.2wt%的Cu、0.95wt%的Si+Fe、0.05wt%的Mn、0.10wt%的Zn、小于0.05wt%的杂质、余量的Al。AA1100铝合金具有极佳的成形加工特性、高耐腐蚀性、良好的焊接性和导电性,广泛用于需要有良好的成形性和高抗蚀性,但强度要求不高的产品,如厨具、小五金件、铝塑复合管等领域。在现有技术中,制备铝塑复合管的一个典型工艺过程包括:制备出厚度约为0.2mm厚度的AA1100铝抗冲击合金板成品后,再将所述铝抗冲击合金板在290℃~400℃、保温17~20小时进行退火,再通过氩弧对接焊制备中间铝管,然后在中间铝管的内外 ...
【技术保护点】
1.一种抗冲击合金板,其特征在于,由以下重量百分比的成分制成:铁:0.15%~0.25%、镁:0.15%~1.80%、铜:1.20%~2.00%、钙:0.40%~1.80%、钛0.2%~0.3%、锌:0.25%~0.75%、镉:≤0.30%、氧化锆:≤0.12%、铅:≤0.03%、铱:≤0.05%、硒:≤0.015%、铂:≤0.010%、其余为铝和不可避免的杂质。
【技术特征摘要】
1.一种抗冲击合金板,其特征在于,由以下重量百分比的成分制成:铁:0.15%~0.25%、镁:0.15%~1.80%、铜:1.20%~2.00%、钙:0.40%~1.80%、钛0.2%~0.3%、锌:0.25%~0.75%、镉:≤0.30%、氧化锆:≤0.12%、铅:≤0.03%、铱:≤0.05%、硒:≤0.015%、铂:≤0.010%、其余为铝和不可避免的杂质。2.根据权利要求1所述的一种抗冲击合金板,其特征在于,由以下重量百分比的成分制成:铁:0.15%、镁:1.2%、铜:1.5%、钙:0.8%、钛0.25%、锌:0.25%、镉:0.18%、氧化锆:0.08%、铅:0.01%、铱:0.03%、硒:0.012%、铂:0.01%...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。