The invention relates to a preparation method of porous polyacrylamide polystyrene composite fibers, which comprises the following steps: 1) mixing polystyrene powder, polyacrylamide powder, dimethylformamide and chlorobenzene, refluxing stirring reaction at 60 75 for 8 12 hours, then cooling to room temperature to obtain PAM/PS spinning solution; 2) electrospinning of PAM/PS spinning solution obtained by step 1, that is, electrospinning. Yes. The composite fiber has the advantages of low cost, high separation flux, acid and alkali resistance, salt resistance and stable structure. Moreover, the highly efficient hydrophobic hydrophobic hydrophobic hydrophobic oil-affinity fiber has good oil recovery and stability in a variety of oil and seawater mixtures. It has broad application prospects in oil-water separation, oil wastewater treatment, oil leakage and other fields.
【技术实现步骤摘要】
多孔聚丙烯酰胺聚苯乙烯复合纤维、制备方法及其应用
本专利技术属于纤维制备
，具体涉及一种多孔聚丙烯酰胺聚苯乙烯复合纤维、制备方法及其应用。
技术介绍
随着社会的快速发展，在工业生产和人们的日常生活中产生大量的含油污水逐渐成为水体环境的重要污染源之一。目前，含油污水的处理一直是一个世界性难题，特别是复杂环境下含油污水的处理。传统油水分离方法主要包括气浮法、离心分离法、吸附和燃烧等，但均存在效率低、成本高、应用范围窄等缺点。利用膜分离技术来实现油水分离被认为是最具有效的分离手段之一。人们开发出许多新型的疏水膜分离材料（如，石墨烯基碳材料、多氟硅烷涂层材料等），可以实现油水的快速分离。大部分的研究报道超疏水分离膜材料，一方面通过高成本材料修饰或者复杂的制备过程构建微纳结构提高疏水性，另一方面通过低表面能有毒的多氟有机物改性降低材料表面能。然而，这些膜材料不仅存在制备过程复杂、成本高、环境毒害性等缺点，而且面对多种复杂的油性污水时，常出现分离通量以及油水分离效率的急剧下降。因此，开发新型强疏水、廉价易得、稳定性高、高油通量的分离膜材料成为实现油水的高效、快速以及稳定...
【技术保护点】
1.一种多孔聚丙烯酰胺聚苯乙烯复合纤维的制备方法，其特征在于，包括如下步骤：1）将聚苯乙烯粉体、聚丙烯酰胺粉体、二甲基甲酰胺和氯苯混合后，于60‑75℃回流搅拌反应8‑12小时，然后冷却至室温，得到PAM/PS纺丝液；2）步骤1）得到的PAM/PS纺丝液经静电纺丝，即得。
【技术特征摘要】
1.一种多孔聚丙烯酰胺聚苯乙烯复合纤维的制备方法，其特征在于，包括如下步骤：1）将聚苯乙烯粉体、聚丙烯酰胺粉体、二甲基甲酰胺和氯苯混合后，于60-75℃回流搅拌反应8-12小时，然后冷却至室温，得到PAM/PS纺丝液；2）步骤1）得到的PAM/PS纺丝液经静电纺丝，即得。2.如权利要求1所述多孔聚丙烯酰胺聚苯乙烯复合纤维的制备方法，其特征在于，步骤1）中，取6.0-15.0g聚苯乙烯粉体、0.10-1.5g聚丙烯酰胺粉体、80-110mL二甲基甲酰胺以及2-8mL氯苯进行...
【专利技术属性】
技术研发人员：王吉超，史维娜，侯玉霞，李英，张裕平，崔增辉，韩维航，陈梦娟，
申请(专利权)人：河南科技学院，新乡学院，
类型：发明
国别省市：河南,41