The invention relates to a culture soil with good permeapermeability, which is mainly composed of the following components: sand 40 100, porporporceramic 20 100, porporporporceramic 20 30, pine pine soil 20 9 30, sodsodsodsoil 8 9 20, bone powder 2 4, calcium superphosphate 2 8209 4, 4 parts, potpotpotassium nitrate 0.8 1.2 9 1.2.2.2 0.2 1.2 0.4, potpotpotpotpotassium dihydrogenpotpotassium phosphate 0.4 8209 1.0.0.0.0.0.0.0.0, ferroferroferroferroferroferroferrous sulfsulfate 0.2 2 0, agar 2 4, vinegar 0.1 0.2. The culture soil of the invention has uniform particle size, good dispersion and excellent air permeability.
【技术实现步骤摘要】
一种透气性能好的培养土
本专利技术涉及植物栽培
，尤其涉及一种透气性能好的培养土。
技术介绍
培养土的透气性能使其重要指标之一，现有的透气性好的培养土密度较大、营养并不全面。
技术实现思路
为了解决上述技术问题，提供一种透气性能特别优异的培养土，本专利技术提供以下技术方案：一种透气性能好的培养土，由以质量份数计的以下成分组成：沙土40-100份、多孔陶瓷20-30份、松针土20-30份、草皮土8-20份、骨粉2-4份、过磷酸钙2-4份、硝酸钾0.8-1.2份、磷酸二氢钾0.4-1.0份、硫酸亚铁0.2-0.4份、铁钠盐0.3-0.5份、轻稀土8-20份、琼脂2-4份、食用醋0.1-0.2份。进一步的，所述草皮土可由松针土代替。进一步的，由以质量份数计的以下成分组成：沙土65份、多孔陶瓷25份、松针土25份、草皮土12.5份、骨粉3份、过磷酸钙3份、硝酸钾1份、磷酸二氢钾0.65份、硫酸亚铁0.3份、铁钠盐0.4份、轻稀土12.5份、琼脂3份、食用醋0.15份。进一步的，由以质量份数计的以下成分组成：沙土50份、多孔陶瓷20份、松针土20份、草皮土10份、骨粉2份、过磷酸钙2份、硝酸钾0.8份、磷酸二氢钾0.5份、、硫酸亚铁0.2份、铁钠盐0.3份、轻稀土10份、琼脂2份、食用醋0.1份。进一步的，由以质量份数计的以下成分组成：沙土80份、多孔陶瓷30份、松针土30份、草皮土15份、骨粉4份、过磷酸钙4份、硝酸钾1.2份、磷酸二氢钾0.8份、硫酸亚铁0.4份、铁钠盐0.5份、轻稀土15份、琼脂4份、食用醋0.2份。本专利技术的培养土粒度均匀、分散性好，透气...
【技术保护点】
1.一种透气性能好的培养土，其特征在于：由以质量份数计的以下成分组成：沙土40‑100份、多孔陶瓷20‑30份、松针土20‑30份、草皮土8‑20份、骨粉2‑4份、过磷酸钙2‑4份、硝酸钾0.8‑1.2份、磷酸二氢钾0.4‑1.0份、硫酸亚铁0.2‑0.4份、铁钠盐0.3‑0.5份、轻稀土8‑20份、琼脂2‑4份、食用醋0.1‑0.2份。
【技术特征摘要】
1.一种透气性能好的培养土，其特征在于：由以质量份数计的以下成分组成：沙土40-100份、多孔陶瓷20-30份、松针土20-30份、草皮土8-20份、骨粉2-4份、过磷酸钙2-4份、硝酸钾0.8-1.2份、磷酸二氢钾0.4-1.0份、硫酸亚铁0.2-0.4份、铁钠盐0.3-0.5份、轻稀土8-20份、琼脂2-4份、食用醋0.1-0.2份。2.如权利要求1所述的一种透气性能好的培养土，其特征在于：所述草皮土可由松针土代替。3.如权利要求1所述的一种透气性能好的培养土，其特征在于：由以质量份数计的以下成分组成：沙土65份、多孔陶瓷25份、松针土25份、草皮土12.5份、骨粉3份、过磷酸钙3份、硝酸钾1份、磷酸二氢钾0.65份、硫酸...
【专利技术属性】
技术研发人员：陈卫军，
申请(专利权)人：丹阳市珥陵镇小潘园茭白专业合作社，
类型：发明
国别省市：江苏,32