The invention relates to a manufacturing method of small-sized circular Ti-Cu composite material with diameter less than 20 mm. The implementation process of the manufacturing method is divided into eight main steps: blank preparation, pipe piercing, coating, heating treatment, drawing, finishing, inspection, packaging and delivery of finished products. The small-sized Ti-Cu composite material manufactured by the invention has firm Ti-Cu metal layer, uniform Ti Ti-Cu cross section, and is profitable. The localization of small-sized Ti-Cu composites with existing equipment as soon as possible has supplemented a class of products for Chinese standards, which not only meets the domestic market demand, but also generates foreign exchange through export, thus creating good economic benefits.
【技术实现步骤摘要】
一种直径小于20mm的小规格圆形钛铜复合材料的制造方法
本专利技术涉及钛铜复合材料制造方法领域，尤其是直径小于20mm的小规格圆形钛铜复合材料的制造方法。
技术介绍
目前用于氯碱工业、电力工业等行业的钛铜复合材料的制造方法主要采用是爆炸复合法、热挤压法等制造方法，钛铜复合材料的国家标准GB/T12769-2003就是采用上述制造方法来制造直径为20-60mm圆形钛铜复合材料，对于直径小于20mm的小规格钛铜复合材料，中国尚无相应的国家标准，国内企业尚不掌握上述一种直径小于20mm的小规格圆形钛铜复合材料的制造方法。
技术实现思路
本专利技术所要解决的是提供一种直径小于20mm的小规格圆形钛铜复合材料的制造方法，使得金属钛层与金属铜层结合紧密，能较好地满足使用要求，可利用现有设备实现小规格圆形钛铜复合材料的国产化，迅速开发及拓展小规格钛铜复合材料的应用市场，达到出口创汇，取得较强的市场竞争力和良好的经济效益。本专利技术为解决上述技术问题，采用的技术方案是：制造过程分为：坯料准备、穿管、涂层、加热处理、拉拔、精整、检验成品包装发货等八个主要步骤。a)坯料准备，选用符合标准要求的钛管、紫铜棒作为坯料。b)穿管，是将钛管内表面和紫铜棒外表面进行清理，然后将铜棒穿于钛管中。c)涂层，是将氧化铝均匀涂在钛管表面上，厚度为0.5-2mm，最佳厚度为1-1.5mm，晾干。d)加热处理，是将涂层晾干后的钛铜棒放置加热炉中，加热温度450-600℃，最佳加热温度550-600℃，保温15-30分钟。e)拉拔，配套适宜的模具，将加热处理的钛铜棒拉拔复合。f)精整，对拉拔制成的钛铜复...
【技术保护点】
1.一种圆形钛铜复合材料的制造方法，尤其是直径小于20mm的小规格圆形钛铜复合材料的制造方法，其特征在于，制造方法的实施步骤分为：a)坯料准备，选用符合标准要求的钛管、紫铜棒作为坯料。b)穿管，将铜棒穿于钛管中。c)涂层，将氧化铝均匀涂在钛管表面上，晾干。d)加热处理，将涂层晾干后的钛铜棒加热至450‑600℃，保温15‑30分钟。e)拉拔，配套适宜的模具，将加热处理的钛铜棒拉拔复合。f)精整，对钛铜复合材料的钛表面去除毛刺，修磨划伤，切除钛铜复合材料的两个端头。g)检验，观察断面复合牢度，钛铜复合材料圆度的均匀性。h)成品包装发货，将经检查合格的钛铜复合材料成品进行包装发货。
【技术特征摘要】
1.一种圆形钛铜复合材料的制造方法，尤其是直径小于20mm的小规格圆形钛铜复合材料的制造方法，其特征在于，制造方法的实施步骤分为：a)坯料准备，选用符合标准要求的钛管、紫铜棒作为坯料。b)穿管，将铜棒穿于钛管中。c)涂层，将氧化铝均匀涂在钛管表面上，晾干。d)加热处理，将涂层晾干后的钛铜棒加...