The invention discloses a water-based single component MDF sealing material, which is composed of 40~50 parts of acrylate emulsion, 5~10 parts of water, 03 to 0.7 parts of gaseous silica, 0.2 to 0.7 parts of dispersant, 0.2 to 1 parts of defoaming agent, 5~15 parts of film forming agent, 0.1 to 0.5 parts of bactericide, 0.1 to 0.5 parts of thickening agent, 1 parts of titanium dioxide and calcium carbonate. The invention provides a water-based one-component MDF sealing material with excellent comprehensive performance, which solves the problems of large odor of oil-based sealing bottom, large VOV emission, short use time, poor adhesion and poor sealing effect of medium fiberboard.
【技术实现步骤摘要】
一种具有水洗白效果的水性单组份MDF封闭材料及其制备方法
本专利技术属于材料领域，具体涉及一种具有水洗白效果的水性单组份MDF封闭材料及其制备方法。
技术介绍
随着科技的不断进步，人们对环境保护越来越重视，家具涂装逐步由传统的油性涂装向水性涂装过渡，也就是“油改水”。原有的“油性”浸涂材料存在气味大、VOV排放大、使用时间短、附着力差、对中纤板封闭效果差等问题。针对现有技术的不足，本领域急需研发一种具有水洗白效果的水性单组份MDF封闭材料，从而拓宽不饱和聚酯底漆的施工宽容性，达到降低环境污染的目的。
技术实现思路
针对现有技术的不足，本专利技术提供一种具有水洗白效果的水性单组份MDF封闭材料及其制备方法。本专利技术的技术目的是通过以下技术方案实现的：本专利技术提供一种具有水洗白效果的水性单组份MDF封闭材料，按重量份计，组成如下：水性树脂45～55份丙烯酸酯乳液40～50份水5～10份气相二氧化硅03～0.7份分散剂0.2～0.7份消泡剂0.2～1份成膜助剂5～15份杀菌剂0.1～0.5份增稠剂0.2～0.5份钛白粉2～5份碳酸钙10～20份滑石粉10～15份。作为本...
【技术保护点】
1.一种具有水洗白效果的水性单组份MDF封闭材料，其特征在于，按重量份计，组成如下：水性树脂45～55份丙烯酸酯乳液40～50份水5～10份气相二氧化硅03～0.7份分散剂0.2～0.7份消泡剂0.2～1份成膜助剂5～15份杀菌剂0.1～0.5份增稠剂0.2～0.5份钛白粉2～5份碳酸钙10～20份滑石粉10～15份。
【技术特征摘要】
1.一种具有水洗白效果的水性单组份MDF封闭材料，其特征在于，按重量份计，组成如下：水性树脂45～55份丙烯酸酯乳液40～50份水5～10份气相二氧化硅03～0.7份分散剂0.2～0.7份消泡剂0.2～1份成膜助剂5～15份杀菌剂0.1～0.5份增稠剂0.2～0.5份钛白粉2～5份碳酸钙10～20份滑石粉10～15份。2.根据权利要求1所述的一种具有水洗白效果的水性单组份MDF封闭材料，其特征在于，所述丙烯酸乳液为万华化学的Lacper4600。3.根据权利要求1所述的一种具有水洗白效果的水性单组份MDF封闭材料，其特征在于，所述水为纯净水，所述气相二氧化硅为非处理型气相白炭黑。4.根据权利要求1所述的一种具有水洗白效果的水性单组份MDF封闭材料其特征在于，所述分散剂为含颜料亲和基团的高分子量嵌段共聚物溶液。5.根据权利要求1所述的一种具有水洗白效果的水性单组份MDF封闭材料其特征在于，所述消泡剂为高相容的脱泡及乳液。6.根据权利要求1所述的一种综合性能优异的水性单组份MDF封闭材料，其特征在于，所述成膜助剂为二丙二醇单甲醚。7.根据权利要求1所述的一种具有水洗白效果的水性单组份MDF封闭材料其特征在于...
【专利技术属性】
技术研发人员：兰春风，汪峻成，麦毅，
申请(专利权)人：成都展辰涂料有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。