This patent invents a flame retardant high impact polystyrene (HIPS) material with good photothermal stability and its preparation method. The HIPS material is mainly composed of bromine flame retardant, Sb2O3 as synergist, bis(1 alkoxy 2,2,6,6 tetramethylpiperidine 4)sebacate as flame retardant synergist with light stabilization. It is prepared by melt mixing and granulation. The composition and mass fraction of each component are as follows: HIPS resin 80.90%, bromine flame retardant 9.15%, Sb2O3 3 3.5%, bis(1 alkoxy 2,2,6,6 tetramethylpiperidine 4)sebacate 0.1.0%, antioxidant 0.0.5%, other processing aids 0.1%. The HIPS materials prepared by the above methods not only have good flame retardant properties, the flame retardant grade can reach UL94 V_0, but also have good photothermal stability, processing and mechanical properties.
【技术实现步骤摘要】
一种具有良好光热稳定性的阻燃高抗冲聚苯乙烯材料及其制备方法
本专利技术涉及一种具有良好光热稳定性的阻燃高抗冲聚苯乙烯材料及其制备方法，具体地说是以溴系阻燃剂为主阻燃剂，Sb2O3为协效剂，双(1-烷氧基-2,2,6,6-四甲基哌啶-4-基)癸二酸酯为兼有光稳定作用的阻燃增效剂，通过熔融混炼、造粒制得的具有良好光热稳定性的阻燃高抗冲聚苯乙烯材料，属高分子材料领域。
技术介绍
高抗冲聚苯乙烯(HIPS)是对聚苯乙烯进行增韧改性得到的一种具有较高的抗冲击强度的聚合物材料。HIPS因具有优异的加工性能、力学性能、电绝缘性能、尺寸稳定性能及价格低廉等优点而广泛用于家用电器、办公设备、仪器仪表、汽车零部件等领域[杜强国，张传贤，何慧.塑料工业手册:苯乙烯系树脂[M].北京:化学工业出版社，2004:198]。但是HIPS属于易燃产品，需要阻燃且阻燃级别较高，一般需要通过UL94V-0级。目前HIPS所用阻燃剂主要是溴系阻燃剂，并以氧化锑为协效剂。常用的溴系阻燃剂有十溴二苯醚(DBDPO)(周健,王玲玲.增韧阻燃高抗冲聚苯乙烯的研制，工程塑料应用,2008,36(2):21-2...
【技术保护点】
1.一种具有良好光热稳定性的阻燃高抗冲聚苯乙烯材料，其特征在于，它以溴系阻燃剂为主阻燃剂，Sb2O3为协效剂，双(1‑烷氧基‑2,2,6,6‑四甲基哌啶‑4‑基)癸二酸酯为兼有光稳定作用的阻燃增效剂，其组成和各组分的质量分数如下：高抗冲聚苯乙烯树脂80‑90％，溴系阻燃剂9‑15％，Sb2O3 3‑5％，双(1‑烷氧基‑2,2,6,6‑四甲基哌啶‑4‑基)癸二酸酯0.1‑1.0％，抗氧剂0.0‑0.5％，其它加工助剂0‑1.0％。
【技术特征摘要】
1.一种具有良好光热稳定性的阻燃高抗冲聚苯乙烯材料，其特征在于，它以溴系阻燃剂为主阻燃剂，Sb2O3为协效剂，双(1-烷氧基-2,2,6,6-四甲基哌啶-4-基)癸二酸酯为兼有光稳定作用的阻燃增效剂，其组成和各组分的质量分数如下：高抗冲聚苯乙烯树脂80-90％，溴系阻燃剂9-15％，Sb2O33-5％，双(1-烷氧基-2,2,6,6-四甲基哌啶-4-基)癸二酸酯0.1-1.0％，抗氧剂0.0-0.5％，其它加工助剂0-1.0％。2.根据权利要求1所述的阻燃高抗冲聚苯乙烯材料，其特征在于，所述的溴系阻燃剂为十溴二苯乙烷和...
【专利技术属性】
技术研发人员：唐林生，刘俊宏，吴鸿志，孙明媚，杨晶巍，徐基海，
申请(专利权)人：青岛科技大学，
类型：发明
国别省市：山东,37