The invention discloses a flexible tactile polypropylene material and its preparation method and application. The flexible tactile polypropylene material consists of 30-50 parts by weight, 20-50 parts by elastomer, 10-30 parts by chopped glass fiber, 4-6 parts by compatibilizer, 0.2-2 parts by auxiliaries, 50-150 g/10 min by melt flow rate of polypropylene, and the elastomer is selected from ethylene. The weight ratio of ethylene-octene copolymer to thermoplastic polyolefin elastomer is 1:1-3. The polypropylene material disclosed by the invention has apparent flexible touch, high rigidity and excellent impact strength at room temperature and low temperature, and can be used for preparing automobile interior parts.
【技术实现步骤摘要】
一种柔性触感聚丙烯材料及其制备方法和应用
本专利技术涉及聚丙烯的材料领域，尤其涉及一种柔性触感聚丙烯材料及其制备方法和应用。
技术介绍
近年来，随着汽车产业的迅猛发展，人们对汽车材料的要求也越来越高。一般而言，汽车内饰材料多用矿物填充聚丙烯，其具有密度低、力学性能优异、成本低以及易于回收利用等优点。但是矿物填充聚丙烯制备的汽车内饰件表面塑料感强，触摸手感不佳，难以带给人一种舒适高档的感觉。现有的解决方法是通过在制件表面覆盖一层高弹性的涂料或是通过蒙皮加工一层软性塑料来实现，但这两种方法增加了生产工序，提高了成本，也难以回收再利用。目前，也有研究从改善原料配方体系的角度来改善触感不佳的问题。如申请公布号为CN105949611A的中国专利文献中公开了一种具有柔性触感的聚丙烯材料，包括重量份的组分：聚丙烯200-300份，成核剂0.4-0.9份，三元乙丙橡胶10-30份，增柔剂15-25份，润滑剂15-25份，二巯基醋酸异辛酯5-10份，聚甲基丙烯酸甲酯5-10份，四甲基哌啶氮氧化物5-10份，硫代二丙酸二月桂酯5-10份，丙三醇5-10份，辅料50-100份；成核剂...
【技术保护点】
1.一种柔性触感聚丙烯材料，其特征在于，按重量份计，原料组成包括：
【技术特征摘要】
1.一种柔性触感聚丙烯材料，其特征在于，按重量份计，原料组成包括：所述聚丙烯的熔体质量流动速率为50～150g/10min；所述弹性体选自乙烯-辛烯共聚物与热塑性聚烯烃弹性体的复合物，乙烯-辛烯共聚物与热塑性聚烯烃弹性体的重量比为1：1～3。2.根据权利要求1所述的柔性触感聚丙烯材料，其特征在于，所述聚丙烯的熔体质量流动速率为80～100g/10min。3.根据权利要求1所述的柔性触感聚丙烯材料，其特征在于，所述乙烯-辛烯共聚物与热塑性聚烯烃弹性体的重量比为1：1～2.5。4.根据权利要求1所述的柔性触感聚丙烯材料，其特征在于，所述乙烯-辛烯共聚物的熔体流动速率为0.5～20g/10min。5.根据权利要求1所述的柔性触感聚丙烯材料，其特征在于，所述热塑性聚烯烃弹性体的熔体流动速率为0.5～10g/10min。6.根据权利要求1所述的柔性触感聚丙烯材料，其特征在于，所述短切玻璃纤维的直径为10～15μm，长度为3～5mm。7.根据权利要求1所述的柔性触感聚...
【专利技术属性】
技术研发人员：周云国，陈晓敏，孙心克，李俊，郑京连，安孝善，
申请(专利权)人：中广核俊尔新材料有限公司，中广核俊尔上海新材料有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。