The invention provides a preparation method of magnesium hydroxide powder, which comprises the following steps: when magnesium hydroxide powder is prepared by hydration reaction of light burned magnesium oxide, magnesium hydroxide powder is prepared by applying pulse current in reaction system. The pulse current applied in the reaction system is 5-1000A, and the pulse frequency used is 50-2000Hz. By adjusting the magnitude and frequency of pulse current, the specific surface area, average particle size and micro-structure morphology of magnesium hydroxide are controlled. Compared with the prior art, the invention has the advantages of simple steps, low cost, easy control of specific surface area, average particle size and micro-structure of magnesium hydroxide.
【技术实现步骤摘要】
一种氢氧化镁粉体的制备方法
本专利技术涉及材料制备技术，尤其涉及一种氢氧化镁粉体的制备方法。
技术介绍
氢氧化镁粉体广泛应用于塑料、橡胶制品阻燃，烟气脱硫，废水处理以及食品添加和材料保温等领域。为了提高氢氧化镁在上述各领域的使用效果，控制氢氧化镁制备过程中的比表面积、平均粒径以及微观组织结构是非常重要的。
技术实现思路
本专利技术的目的在于，针对目前氢氧化镁性能仍有待提高的问题，提出一种氢氧化镁粉体的制备方法，该方法制备的氢氧化镁比表面积、平均粒径以及微观组织结构便于控制。为实现上述目的，本专利技术采用的技术方案是：一种氢氧化镁粉体的制备方法，包括以下步骤：利用轻烧氧化镁通过水化反应制备氢氧化镁粉体时，通过对反应体系内施加脉冲电流的方法制备氢氧化镁粉体，该方法制备的氢氧化镁粉体比表面积、平均粒径和微观组织形貌便于控制。进一步地，施加在反应体系内的脉冲电流大小为5～1000A，使用的脉冲频率为50～2000Hz。进一步地，所述脉冲电流大小为100～500A，使用的脉冲频率为100～1000Hz。进一步地，所述脉冲时间为1-10h，优选为3-8h。进一步地，氢氧化镁粉体的...
【技术保护点】
1.一种氢氧化镁粉体的制备方法，其特征在于，包括以下步骤：利用轻烧氧化镁通过水化反应制备氢氧化镁粉体时，通过对反应体系内施加脉冲电流的方法制备氢氧化镁粉体。
【技术特征摘要】
1.一种氢氧化镁粉体的制备方法，其特征在于，包括以下步骤：利用轻烧氧化镁通过水化反应制备氢氧化镁粉体时，通过对反应体系内施加脉冲电流的方法制备氢氧化镁粉体。2.根据权利要求1所述氢氧化镁粉体的制备方法，其特征在于，施加在反应体系内的脉冲电流大小为5～1000A，使用的脉冲频率为50～2000Hz。3.根据权利要求2所述氢氧化镁粉体的制备方法，其特征在于，所述脉冲电流大小为100～500A，使用的脉冲频率为100～1000Hz。4.根据权利要求1所述氢氧化镁粉体的制备方法，其特征在于，所述脉冲时间为1-10h。5.根据权利要求1所述氢氧化镁粉体的制备方法，其特征在于，氢氧化镁粉体的制备方法，包...
【专利技术属性】
技术研发人员：郑岐，王洪英，平振丰，
申请(专利权)人：中民驰远实业有限公司，
类型：发明
国别省市：辽宁,21