The invention discloses a decontamination and rust remover for aluminum shell battery shell and a preparation method and application thereof. In the mass calculation, a new type of aluminum shell battery shell decontamination and rust remover is prepared by mixing 5%, 10% of the perfume, 5% of 10% of the carbonate, two of sodium carbonate, 5% of 20% of sodium hydroxide, 10% of 20% water, and the remaining amount of aluminum degreasing cleaning agent. Good, it can quickly and easily remove the fouling and electrolyte crystallization of the battery shell, effectively solve the pollution or corrosion problems caused by the sputtering of electrolyte in the aluminum shell battery shell, clean the fouling effect is good, and the cost of materials is low.
【技术实现步骤摘要】
一种铝壳电池外壳去污除锈剂及其制备方法与应用
本专利技术涉及去污除锈剂的制备
，尤其涉及一种铝壳电池外壳去污除锈剂及其制备方法与应用。
技术介绍
电池壳体的表面清洗，一直以来都是困扰电池电芯行业的一大难题，尤其是以铝壳为外壳的动力电池，其壳体表面为PA层，在进行注液及补液时，电解液溅在电池盖板、极组、防爆阀等表面上时间久后，由于电解液及其污垢与PA层的壳体有一定的亲和力，能较强的粘附在铝壳电池外表面，若不能有效的进行清洁清理，外壳表面腐蚀并且污染会逐渐严重，不仅影响电池的外观，若不及时处理，尤其是在高湿度的条件下，还会导致电解液产生的氢氟酸灯腐蚀铝层，引起电池漏液或鼓气，破坏电池的电性能等更为严重的问题。因此，一种有效的铝壳电池外壳的去污除锈剂的研究值得探讨。
技术实现思路
专利技术目的：为了克服现有技术中存在的问题，本专利技术提出了一种铝壳电池外壳去污除锈剂及其制备方法与应用，有效解决了铝壳电池外壳由于电解液溅射产生的污染或腐蚀问题，清洁去污效果好，且用料成本低廉。技术方案：为了解决上述技术问题，本专利技术所采用的技术方案为：一种铝壳电池外壳去污除锈剂，以质量...
【技术保护点】
1.一种铝壳电池外壳去污除锈剂，其特征在于以质量计算包括以下原料：5％‑10％的松香水、5％‑10％的碳酸二甲酯、5％‑20％的氢氧化钠、10％‑20％的水以及50％‑75％的铝材脱脂清洗剂。
【技术特征摘要】
1.一种铝壳电池外壳去污除锈剂，其特征在于以质量计算包括以下原料：5％-10％的松香水、5％-10％的碳酸二甲酯、5％-20％的氢氧化钠、10％-20％的水以及50％-75％的铝材脱脂清洗剂。2.根据权利要求1所述的铝壳电池外壳去污除锈剂，其特征在于以质量计算包括以下原料：5％的松香水、10％的碳酸二甲酯、20％的氢氧化钠、10％-20％的水50％-75％的铝材脱脂清洗剂。3.根据权利要求1或2所述的铝壳电池外壳去污除锈剂，其特征在于所述铝材脱脂清洗剂以质量计算包括10％的柠檬酸，10％的氯化钠，5％的脂肪醇、10％的聚氧乙烯迷，5％的磷酸三钠，10％的渗透剂，10％的油污抓爬剂、余量的...