The invention discloses a method for preparing nickel (Ni) coating on Ti 45Al 8.5Nb alloy surface, which belongs to the field of surface modification of titanium-aluminium alloy materials, and specifically relates to a method for preparing Ni coating on the surface of titanium-aluminium alloy. The method of the invention combines the advantages of high melting point nickel (Ni) coated on the surface of Ti 45Al 8.5Nb alloy by double glow plasma alloying technology, such as high temperature, high strength, corrosion resistance, etc., so as to widen the application range of Ti-Al alloy. The main steps are as follows: Firstly, the prepared Ti_ 45Al_ 8.5Nb alloy is placed in a double glow plasma infiltration furnace, and Ni plate is used as sputtering target material. By adjusting the process parameters of double glow plasma infiltration, different forms of Ni coatings can be prepared. The method has the advantages of simple operation, high efficiency and strong feasibility.
【技术实现步骤摘要】
一种在Ti-45Al-8.5Nb合金表面制备Ni涂层的方法
本专利技术属于钛铝合金表面改性领域，是通过表面防护涂层制备技术在Ti-45Al-8.5Nb合金表面形成Ni涂层，该方法操作简单，可调节参数多，制备出的涂层均匀，致密，无裂缝，与Ti-45Al-8.5Nb合金结合牢固。
技术介绍
钛铝合金属于轻质合金，由于具有低密度、高的比强度，高弹性模量以及高的抗蠕变性能等良好的综合力学性能，因而被广泛应用在航空，航海，汽车，医学等领域。随着国内外学者对钛铝合金的研究，他们将γ-TiAl合金分为两大类，分别是普通Ti-Al合金和高温Ti-Al合金。其中高温Ti-Al合金是以高Nb含量为特征，一般Nb含量在5%以上，与普通Ti-Al合金相比，高Nb钛铝合金的优势在于它的密度变化不大，约为4.3g/cm3是传统镍基高温合金的一半，但由于加入Nb以后提高了钛铝合金的固相线，使钛铝合金的工作温度提高60-100℃，接近传统镍基高温合金的使用温度，强度提高300-500Mpa，抗蠕变性能也得到提高，此外高Nb钛铝合金的显微组织和普通钛铝合金基本相同，因此有非常广阔的应用前景。然而高...
【技术保护点】
1.一种在Ti‑45Al‑8.5Nb合金表面制备Ni涂层的方法，其特征是包括以下步骤：首先通过真空电弧炉制备Ti‑45Al‑8.5Nb合金，然后通过双层辉光离子渗金属技术渗入Ni金属，使Ti‑45Al‑8.5Nb合金表面形成Ni涂层。
【技术特征摘要】
1.一种在Ti-45Al-8.5Nb合金表面制备Ni涂层的方法，其特征是包括以下步骤：首先通过真空电弧炉制备Ti-45Al-8.5Nb合金，然后通过双层辉光离子渗金属技术渗入Ni金属，使Ti-45Al-8.5Nb合金表面形成Ni涂层。2.如权利要求1所述的一种在Ti-45Al-8.5Nb合金表面制备Ni涂层的方法，其特征在于，选用的基体合金为Ti-45Al-8.5Nb合金，通过对合金...