The invention relates to a preparation method of a novel polyurethane composite rope, which belongs to the field of polyurethane foaming and consists of components A and B. Component A is prepared from the following raw materials: modified amine curing agent 5 100 1000, polyether 100 1000, MDI: 50 400, anti-ultraviolet agent 5 25, epoxy resin 50 500, hydroxybutadiene 100 1000, and component B is composed of modified amine curing agent 5 100 1000 The following raw materials are prepared: 1,4-butanediol 5-30 copies, toughener 5-30 copies, carbon fiber material 200-1000 copies. The new composite rope prepared by the invention has strong anti-aging performance, strong corrosion resistance and wear resistance, and long service life. The product of the invention has good tensile property, is not easy to break under large load, and is tough and durable.
【技术实现步骤摘要】
新型聚氨酯复合材料绳索的制备方法
本专利技术涉及一种新型聚氨酯复合材料绳索的制备方法，属于聚氨酯发泡领域。
技术介绍
当前的绳索材料主要分为两大类，一类是以金属材料为基础的钢丝绳，一类是以高强度聚丙烯、超高分子量聚乙烯和芳纶纤维等等高分子材料为基础的有机高分子绳索。钢丝绳强度高，比较抗蠕变，但刚度大不易打结，长时间使用后，在大载荷下常常断裂。有机高分子绳索柔软性强，易于运输，便于打结使用，但抗蠕变性差，野外使用易老化，耐腐耐磨性差，使用寿命短。本专利旨在研究一种新型复合材料绳索，抗老化，耐腐耐磨性能强，使用寿命长。
技术实现思路
根据现有技术的不足，本专利技术要解决的技术问题是：提供一种新型聚氨酯复合材料绳索的制备方法，生产的产品抗老化，耐腐耐磨性能强，使用寿命长。本专利技术解决其技术问题所采用的技术方案是：提供一种新型聚氨酯复合材料绳索的制备方法，由A，B组份构成，其中A组份由以下原料制备而成：改性胺固化剂5-100份，聚醚100-1000份，MDI50-400份，抗紫外线剂5-25份，环氧树脂50-500份，端羟基丁二烯100-1000份组成，B组份由以下原料制备...
【技术保护点】
1.一种新型聚氨酯复合材料绳索的制备方法，其特征在于由A和B两组份构成，其中A组份由以下原料制备而成：改性胺固化剂 5‑100份，聚醚 100‑1000份，MDI 50‑400份，抗紫外线剂 5‑25份，环氧树脂 50‑500份，端羟基丁二烯 100‑1000份组成，B组份由以下原料制备而成：1，4‑丁二醇 5‑30份，增韧剂 5‑30份，碳纤维材料 200‑1000份。
【技术特征摘要】
1.一种新型聚氨酯复合材料绳索的制备方法，其特征在于由A和B两组份构成，其中A组份由以下原料制备而成：改性胺固化剂5-100份，聚醚100-1000份，MDI50-400份，抗紫外线剂5-25份，环氧树脂50-500份，端羟基丁二烯100-1000份组成，B组份由以下原料制备而成：1，4-丁二醇5-30份，增韧剂5-30份，碳纤维材料200-1000份。2.根据权利要求1所述的新型聚氨酯复合材料绳索的制备方法，其特征在于所...