The formulation of an ABS antimicrobial sheet is characterized by: ABS resin, glass fiber, nano-titanium dioxide, the mass ratio of glass fiber to ABS resin (22-30):80, the mass ratio of nano-titanium dioxide to ABS resin (0.3-3):80, and the mass ratio of additives to ABS resin (1-4):100. Beneficial effects of the invention are as follows: the invention realizes the antimicrobial functionalization of ABS sheet by adding nano-titanium dioxide into general-purpose ABS resin, opens up a new method for the preparation and production of ABS sheet by using the strength of glass fiber reinforced ABS sheet, and has important application value for the present situation of producing ABS sheet with special ABS resin for torsion, and has important application value in electronic appliances, automotive parts and furniture. There are good market prospects in the fields of sanitary ware, industrial parts and so on.
【技术实现步骤摘要】
一种ABS抗菌板材的配方及其制造工艺
本专利技术涉及一种ABS抗菌板材的配方及其制造工艺，属于新材料和材料合成与制备
技术介绍
ABS树脂是重要的通用合成树脂，具有抗冲击强度高、耐热和耐低温性能好、耐化学腐蚀、表面硬度高、容易成型加工等优点，广泛用于电子电器、汽车零部件、家具、卫浴和工业零件等领域。虽然中国为世界ABS树脂第一生产大国，但多为通用级ABS树脂，ABS专用树脂如阻燃、透明、高光泽、消光、耐候、抗菌、导电等主要依赖进口，生产成本较高。ABS板材是ABS树脂产品的基础材料。目前，ABS板材的制备方法主要是ABS专用树脂的挤压成型工艺，且研究领域主要集中在专用树脂的制备与改性，如板材级ABS树脂的研究开发(塑料科技，2010(3)-77-81)，板材用ABS树脂改性及其加工应用(工程塑料应用，2009(12)-30-33)，一种低烟阻燃PC/ABS合金板材专用料(工程塑料应用，2007，35(8)-77-77)，以及专利技术专利：一种汽车用ABS挤出板材材料及其制备方法(申请号：200910200576.1)。目前有用ABS树脂制备工程塑料(AB...
【技术保护点】
1.一种ABS 抗菌板材的配方，其特征在于：包括ABS 树脂、玻璃纤维、纳米TiO2，玻璃纤维与ABS 树脂的质量比为(22 ～ 30) ∶ 80，纳米TiO2 与ABS树脂的质量比为(0.3～ 3) ∶80，添加剂与ABS 树脂的质量比为(1 ～ 4) ∶ 100。
【技术特征摘要】
1.一种ABS抗菌板材的配方，其特征在于：包括ABS树脂、玻璃纤维、纳米TiO2，玻璃纤维与ABS树脂的质量比为(22～30)∶80，纳米TiO2与ABS树脂的质量比为(0.3～3)∶80，添加剂与ABS树脂的质量比为(1～4)∶100。2.根据权利要求1所述的一种ABS抗菌板材的配...
【专利技术属性】
技术研发人员：孙宏立，
申请(专利权)人：慈溪清泉电器有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。