The invention relates to a flame retardant and toughening plastic, which is mainly composed of 45 55 copolymer of styrene and acrylonitrile, 2 10 copolymer of acrylate, 0.2 2.5 copolymer of flame retardant, 5 15 copolymer of toughening agent, 0.1 0.3 copolymer of antioxidant, 0.5 3.5 copolymer of diallyl compound, 2 10 copolymer of acrylic acid processing aids, 2 10 copolymer of crosslinking agent and phosphorous chelating agent. 0.3 0.4 phr of agent, 0.5 5 phr of acrylate adhesive, 0.5 0.8 phr of polyolefin, 0.05 0.15 phr of auxiliary antioxidant, 0.5 0.6 phr of cobalt octanate. The plastic of the invention has the advantages of good flame retardancy and super toughness.
【技术实现步骤摘要】
一种阻燃增韧塑料
本专利技术涉及高分子材料
，尤其涉及一种阻燃增韧塑料。
技术介绍
随着塑料制品的广泛使用，其阻燃性能的要求也越来越高，同时，对韧性的要求也越来越高。
技术实现思路
为了解决上述技术问题，提供一种阻燃性能好、韧性强的塑料制品，本专利技术提供以下技术方案：一种阻燃增韧塑料，由以质量份数计的以下成分组成：苯乙烯-丙烯腈共聚物45-55份、丙烯酸酯胶黏剂2-10份、阻燃剂0.2-2.5份、增韧剂5-15份、抗氧剂0.1-0.3份、二烯丙基化合物0.5-3.5份、全丙烯酸加工助剂2-10份、交联剂2-10份、亚磷酸酯螯合剂0.3-0.4份、丙烯酸酯胶黏剂0.5-5份、聚烯烃0.5-0.8份、辅助抗氧剂0.05-0.15份、辛酸钴0.5-0.6份。进一步的，所述阻燃剂由壳聚糖代替。进一步的，所述全丙烯酸加工助剂用三元乙丙橡胶代替。进一步的，所述丙烯酸酯胶黏剂由水玻璃代替。本专利技术的塑料具有阻燃性好、韧性超强的优点。具体实施方式实施例1、一种阻燃增韧塑料，由以质量份数计的以下成分组成：苯乙烯-丙烯腈共聚物50份、丙烯酸酯胶黏剂6份、阻燃剂1份、增韧剂10份、抗氧剂0.2份、二烯丙基化合物2份、全丙烯酸加工助剂3份、交联剂6份、亚磷酸酯螯合剂0.35份、丙烯酸酯胶黏剂2.5份、聚烯烃0.65份、辅助抗氧剂0.1份、辛酸钴0.55份。实施例2、一种阻燃增韧塑料，由以质量份数计的以下成分组成：苯乙烯-丙烯腈共聚物45份、丙烯酸酯胶黏剂3份、阻燃剂0.5份、增韧剂5份、抗氧剂0.1份、二烯丙基化合物0.5份、全丙烯酸加工助剂5份、交联剂2份、亚磷酸酯螯合剂...
【技术保护点】
1.一种阻燃增韧塑料，其特征在于：由以质量份数计的以下成分组成：苯乙烯‑丙烯腈共聚物45‑55份、丙烯酸酯胶黏剂2‑10份、阻燃剂0.2‑2.5份、增韧剂5‑15份、抗氧剂0.1‑0.3份、二烯丙基化合物0.5‑3.5份、全丙烯酸加工助剂2‑10份、交联剂2‑10份、亚磷酸酯螯合剂0.3‑0.4份、丙烯酸酯胶黏剂0.5‑5份、聚烯烃0.5‑0.8份、辅助抗氧剂0.05‑0.15份、辛酸钴0.5‑0.6份。
【技术特征摘要】
1.一种阻燃增韧塑料，其特征在于：由以质量份数计的以下成分组成：苯乙烯-丙烯腈共聚物45-55份、丙烯酸酯胶黏剂2-10份、阻燃剂0.2-2.5份、增韧剂5-15份、抗氧剂0.1-0.3份、二烯丙基化合物0.5-3.5份、全丙烯酸加工助剂2-10份、交联剂2-10份、亚磷酸酯螯合剂0.3-0.4份、丙烯酸酯胶黏剂0.5-5份、聚...