The invention discloses a corrosion-resistant stirring leaf, which comprises a stirring shaft and a stirring blade. The stirring blade is evenly arranged on the stirring shaft. The outer surface of the stirring blade is provided with a corrosion-resistant coating layer. The corrosion-resistant coating layer consists of the following raw materials by weight: phenolic epoxy resin 30 40 parts, polyvinyl formaldehyde 5 15 parts, nano alumina 5 10 parts, aluminium silicate 2 15 parts. Among them, 10 25 kaolin and 10 35 deionized water. The invention has reasonable design, corrosion resistant coating layer is arranged on the mixing blade, the corrosion resistance and bending ability of the mixing blade are improved, and the service life of the mixing blade is prolonged.
【技术实现步骤摘要】
耐腐蚀搅拌叶
本专利技术涉及一种搅拌叶，特别涉及一种耐腐蚀搅拌叶。
技术介绍
金属腐蚀不仅给人类带来经济上的损失，而且不利于自然资源和环境保护，有时甚至危及人身安全。为了防止和减缓腐蚀，在生产实践和科学实验中开发了许多防腐蚀的方法，其中以涂料保护最为方便、经济，因而得到了广泛的应用。
技术实现思路
本专利技术的目的就在于提供一种设计合理，制作成本较低，使用寿命长的耐腐蚀搅拌叶。为了实现上述目的，本专利技术采用的技术方案是这样的：本专利技术的耐腐蚀搅拌叶，包括搅拌轴和搅拌叶片，所述搅拌叶片均匀排布在搅拌轴上，所述搅拌叶片外表面设有耐腐蚀涂料层，所述耐腐蚀涂料层按重量份由以下原料组成：酚醛环氧树脂30-40份、聚乙烯醇缩甲乙醛5-15份、纳米氧化铝5-10份、硅酸铝2-15份、高岭土10-25份、去离子水10-35份。进一步，所述耐腐蚀涂料层厚度大于20μm。进一步，所述搅拌叶片与搅拌轴端面的可弯曲角度为0°-30°。与现有技术相比，本专利技术的优点在于：本专利技术设计合理，搅拌叶片上设置耐腐蚀涂料层，提高了搅拌叶的耐腐蚀能力和弯曲能力，延长了搅拌叶的使用寿命。附图说明图1为本专利技术的结构示意图。具体实施方式下面将结合附图对本专利技术作进一步说明。参见图1，本专利技术的耐腐蚀搅拌叶，包括搅拌轴1和搅拌叶片2，所述搅拌叶片2均匀排布在搅拌轴1上，所述搅拌叶片2外表面设有耐腐蚀涂料层3，所述耐腐蚀涂料层3按重量份由以下原料组成：酚醛环氧树脂30-40份、聚乙烯醇缩甲乙醛5-15份、纳米氧化铝5-10份、硅酸铝2-15份、高岭土10-25份、去离子水10-35份，所述...
【技术保护点】
1.一种耐腐蚀搅拌叶，其特征在于：包括搅拌轴和搅拌叶片，所述搅拌叶片均匀排布在搅拌轴上，所述搅拌叶片外表面设有耐腐蚀涂料层，所述耐腐蚀涂料层按重量份由以下原料组成：酚醛环氧树脂30‑40份、聚乙烯醇缩甲乙醛5‑15份、纳米氧化铝5‑10份、硅酸铝2‑15份、高岭土10‑25份、去离子水10‑35份。
【技术特征摘要】
1.一种耐腐蚀搅拌叶，其特征在于：包括搅拌轴和搅拌叶片，所述搅拌叶片均匀排布在搅拌轴上，所述搅拌叶片外表面设有耐腐蚀涂料层，所述耐腐蚀涂料层按重量份由以下原料组成：酚醛环氧树脂30-40份、聚乙烯醇缩甲乙醛5-15份、纳米氧化铝5-10份、硅...