The invention discloses a high strength and low percolation UHMWPE/superconducting carbon black conductive composite material and a preparation method thereof. The components include 85-98.8 parts of UHMWPE powder, 1-14.8 parts of superconducting carbon black, 0.1-0.6 parts of antioxidant and 0.1-0.6 parts of coupling agent. The preparation process is as follows: raw material drying; high-speed mixing preparation of UHMWPE / superconducting carbon black blend particles; high-temperature compaction molding. The UHMWPE/superconducting carbon black conductive composite material provided by the invention has high strength and low percolation. When the content of superconducting carbon black is 1 wt%, the conductivity can reach 10%.
【技术实现步骤摘要】
一种高强度低逾渗UHMWPE/超导炭黑导电复合材料及其制备方法
本专利技术属于一种高强度低逾渗UHMWPE/超导炭黑导电复合材料的制备方法。
技术介绍
随着电子电器设备的进一步发展，聚合物导电复合材料的应用继而得到了快速的发展。超高分子量聚乙烯有很多优良的性能，如耐磨损性、耐冲击、耐化学腐蚀性、自润滑性等，存在的许多不足：热变形温度低、硬度低、强度低、耐温性能差、熔融粘度高、流动性差等缺点，限制了其应用，进行其UHMWPE的改性，改性方法主要有物理改性(填充改性)、化学改性(共聚改性、交联改性和交联等)和聚合物共混改性，通过改性可改善UHMWPE本身的缺陷，提高耐热性、阻燃、抗静电等方面的特性。超高分子量聚乙烯的高性能化、工程塑料化、功能化是聚合物复合材料研究领域最重要的追求目标之一。UHMWPE因表面电阻率为ρs=1016～1017Ω,体积电阻率ρv=1017～1018Ω•cm,介电常数为ε=2.2～2.3。在使用过程会因摩擦形成电荷聚集现象，产生静电放电，静电放电会引起火灾等安全隐患，限制了UHMWPE管材在某些特殊的矿业的应用，因此对于UHMWPE管材进行抗...
【技术保护点】
1.一种高强度低逾渗UHMWPE/超导炭黑导电复合材料，其特征在于，由下述重量配比的原料制成：UHMWPE粉料85～98.8份、超导炭黑1～14.8份、抗氧剂0.1~0.6份，偶联剂0.1～0.6份。
【技术特征摘要】
1.一种高强度低逾渗UHMWPE/超导炭黑导电复合材料，其特征在于，由下述重量配比的原料制成：UHMWPE粉料85～98.8份、超导炭黑1～14.8份、抗氧剂0.1~0.6份，偶联剂0.1～0.6份。2.根据权利要求1所述的一种高强度低逾渗UHMWPE/超导炭黑导电复合材料，其特征在于，所述UHMWPE粉料为粒径分布范围30~200μm，数均分子量为300~800万g/mol，拉伸强度≥38MPa的粉料。3.根据权利要求1所述的一种高强度低逾渗UHMWPE/超导炭黑导电复合材料，其特征在于，所述超导炭黑，品牌：亿博瑞，型号：F900A，氮吸附比表面750~1100m2/Kg，DBP吸收值450ml/g，粒径范围9~17nm。经过偶联剂表面处理，其制备方法为：将超导炭黑与偶联剂按质量比为10：0.6~1称量，保持转速600~2000rpm，高速搅拌5~30min，所述偶联剂为硅烷偶联剂或钛酸酯偶联剂。4.权利要求1-3任一所述的一种高强度低逾渗UH...
【专利技术属性】
技术研发人员：钱庆荣，成惠斌，陈庆华，黄宝铨，杨松伟，刘任嫔，肖荔人，
申请(专利权)人：福建师范大学，
类型：发明
国别省市：福建,35