The invention discloses a zero-degree silica gel coating, which comprises the following components by weight: 20-40 parts of methyl vinyl polysiloxane, 5-10 parts of methyl hydrogen silicone oil, 3-7 parts of methyl phenyl vinyl polysiloxane, 0.2-2 parts of inhibitor, 0.2-2 parts of siloxane coupling agent, 8-20 parts of white carbon black, 30-50 parts of weight. Organic solvents, metal catalysts of 1-5 parts by weight, and preparation methods thereof are also disclosed. When the coating is applied on the surface of zero degree silica gel products, the coating can achieve matte effect and silk-slip handle, and has excellent adhesion, heat resistance, water resistance, corrosion resistance, friction resistance and UV aging resistance.
【技术实现步骤摘要】
一种零度硅胶用涂料及其制备方法
本专利技术涉及涂料
，具体涉及一种零度硅胶用涂料及其制备方法。
技术介绍
邵氏硬度在20A以下的硅胶产品可称为零度硅胶产品，该产品具有优异的软度和弹性，并且无毒环保，手感细腻柔软宛如婴儿的肌肤一样。零度硅胶产品广泛应用于护膝、护腕等运动护具以及仿真玩具、医学教学、医疗设备等领域。由于加入过量的硅油，零度硅胶产品表面手感略微阻涩，并且容易析油，阻碍了零度硅胶产品的大面积推广使用。为解决这一问题，可以在零度硅胶产品上涂覆一层涂料，使其长期拥有细腻的外观及丝滑的手感。然而，常规的硅胶涂料需要添加一定量的二氧化硅作为消光剂，其易被零度硅胶产品表面析出的硅油吸收，从而使涂层失去暗哑的外观，而且严重影响手感及涂层的牢度，易造成涂层脱落。
技术实现思路
针对现有技术的上述不足，本专利技术的目的之一是提供一种零度硅胶用涂料，通过有机硅树脂、硅油及助剂的合理搭配，使涂层具有优异的附着力、细腻的外观和丝滑的手感。为实现上述目的，本专利技术采用的技术方案是：一种零度硅胶用涂料，包括以下按重量份计的组分：20～40重量份的甲基乙烯基聚硅氧烷、5～10重量...
【技术保护点】
1.一种零度硅胶用涂料，其特征在于，包括以下组分：20～40重量份的甲基乙烯基聚硅氧烷、5～10重量份的甲基含氢硅油、3～7重量份的甲基苯基乙烯基聚硅氧烷、0.2～2重量份的抑制剂、0.2～2重量份的硅氧烷偶联剂、8～20重量份的白炭黑、30～50重量份的有机溶剂、1～5重量份的金属催化剂。
【技术特征摘要】
1.一种零度硅胶用涂料，其特征在于，包括以下组分：20～40重量份的甲基乙烯基聚硅氧烷、5～10重量份的甲基含氢硅油、3～7重量份的甲基苯基乙烯基聚硅氧烷、0.2～2重量份的抑制剂、0.2～2重量份的硅氧烷偶联剂、8～20重量份的白炭黑、30～50重量份的有机溶剂、1～5重量份的金属催化剂。2.根据权利要求1所述的零度硅胶用涂料，其特征在于，所述甲基乙烯基聚硅氧烷的数均分子量为5～20万。3.根据权利要求1或2所述的零度硅胶用涂料，其特征在于，所述甲基乙烯基聚硅氧烷的乙烯基含量为0.1～0.3％。4.根据权利要求1所述的零度硅胶用涂料，其特征在于，所述甲基含氢硅油的含氢量为0.5～1.5％。5.根据权利要求1所述的零度硅胶用涂料，其特征在于，所述甲基苯基乙烯基聚硅氧烷的...
【专利技术属性】
技术研发人员：潘峰，李平，王卫国，缪培凯，吕国强，杨波，符饶生，凌云剑，伍松，
申请(专利权)人：湖南松井新材料股份有限公司，
类型：发明
国别省市：湖南,43
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。