The invention discloses a PP pipe production process, which is divided into unsaturated polyester 47 55%, talc powder 25 28%, nanopowder 12 15%, CPE2 3%, stabilizer 2 8209 4%, paraffin 0.4 8209 0.5%, methyl ethyl ketone 0.3 8209 0.4%, paraffin 0.4%, PEwax 0.25 8209 0.3%, rutile titanite powder 0.5 8209 0 0.5 0 0.0 0.8%, 0.8%, chlorinated PPsilane 0.7 8209 1%, OB OB 0.01 0.01, OBOBOB0 0 0 0 0 0.01 0.01, OB0.01 additive 0.01 0.01, OB0.01 0 Titanium Titanium dioxide 0.2 0.4%. The material of the invention is made by mixing the above materials and stirring evenly. The nano-powder is used to replace light calcium carbonate powder, and the PE wax is used to replace dioctyl ester. Combining with the modern production process, the invention has the advantages of low cost and high surface finish of the product.
【技术实现步骤摘要】
一种PP管材的生产工艺
本专利技术涉及化工领域,具体的是涉及该领域内的一种PP材料。
技术介绍
使用PP管取代铸铁管和镀锌管已经成为市场发展的趋势,但是现有技术中用于制作管件的PP材料存在生产成本高和表面光洁度底的问题。
技术实现思路
为解决现有技术方案的缺陷,本专利技术公开了一种成本低廉、表面光洁度高的PP材料。本专利技术公开了一种PP材料,按质量百分比分为:不饱和聚酯47-55%、滑石粉25-28%、纳米粉12-15%、CPE2-3%、稳定剂2-4%、石蜡0.4-0.5%、甲基乙基酮0.3-0.4%、PE蜡0.25-0.3%、金红石钛白粉0.5-0.8%、氯化PP硅烷0.7-1%、OB增白剂0.01-0.02%、锐钛型钛白粉0.2-0.4%,本专利技术材料是将上述材料混合后,搅拌均匀制得。本专利技术的一种PP管材的生产工艺,用于生产各种排水管具有成本低廉、表面光洁度高的优点。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本专利技术。实施例一根据比例,以不饱和聚酯取100g为基数,余下材料的所需质量为:滑石粉50g、纳米粉25g、CPE4g、稳定剂3.4g、石蜡0.8g、甲基乙基酮0.6g、PE蜡0.5g、金红石钛白粉1g、氯化PP硅烷1.5g、OB增白剂0.02g、锐钛型钛白粉0.4g,本专利技术材料是将上述材料混合后,搅拌均匀制得,适合排水管的制造。在PP排水管材生产过程中,以往配方中所使用的钙粉与二辛脂价格昂贵且生产出的产品表面光洁度不高,上述配方中使用纳米粉取代轻质碳钙粉,使用PE蜡取 ...
【技术保护点】
1.一种PP管材的生产工艺,由下列原料组成,其特征在于:按质量百分比分为,不饱和聚酯47‑55%、滑石粉25‑28%、纳米粉12‑15%、CPE2‑3%、稳定剂2‑4%、石蜡0.4‑0.5%、甲基乙基酮0.3‑0.4%、PE蜡0.25‑0.3%、金红石钛白粉0.5‑0.8%、氯化PP硅烷0.7‑1%、OB增白剂0.01‑0.02%、锐钛型钛白粉0.2‑0.4%。
【技术特征摘要】
1.一种PP管材的生产工艺,由下列原料组成,其特征在于:按质量百分比分为,不饱和聚酯47-55%、滑石粉25-28%、纳米粉12-15%、CPE2-3%、稳定剂2-4%、石蜡0.4-0.5%、甲基乙基酮0.3-0.4%、PE蜡0.25-0.3%、金红石钛白粉0.5-0.8%、氯化PP硅烷0.7-1%、OB增白剂0.01-0.02%、锐钛型钛白粉0.2-0.4%。2.根据权利要求1中所述的一种PP管材的生产工艺,其特征在于:根据比例,以不饱和聚酯取100g为基数,余...