本发明专利技术提供一种环保型耐高温橡胶增塑材料。本发明专利技术的耐高温橡胶增塑材料，由以下重量份数的物质组成：三甘油酯：80‑120份；二甲基甲酰胺：80‑120份；己二酸二辛酯：30‑70份；抗氧剂：1‑2份。按照上述重量比取三甘油酯；二甲基甲酰胺；己二酸二辛酯；抗氧剂，加入到反应釜中，进行聚酯化反应，再经减压蒸馏即可。本发明专利技术生产的耐高温橡胶增塑材料拥有优异的耐热性、耐老化性、耐油、耐溶剂性能。

High Temperature Resistant Rubber Plasticizer and Its Preparation Method

The invention provides an environmentally friendly high temperature resistant rubber plasticizing material. The high temperature resistant rubber plasticizing material of the present invention consists of triglyceride: 80 120 parts by weight; dimethylformamide: 80 120 parts; dioctyl adipate: 30 70 parts; and antioxidant: 1 2 parts. According to the above weight ratio, triglyceride, dimethylformamide, dioctyl adipate and antioxidant are added to the reactor for polyesterification and then vacuum distillation. The high temperature resistant rubber plasticizer produced by the invention has excellent heat resistance, aging resistance, oil resistance and solvent resistance.

【技术实现步骤摘要】
耐高温橡胶增塑材料及其制备方法
本专利技术涉及一种耐高温橡胶增塑材料及其制备方法，属于橡胶助剂

技术介绍
增塑剂是大宗工业品，广泛应用于国民经济各领域，包括塑料、橡胶、粘合剂、纤维素、树脂、医疗器械、电缆等成千上万种产品中。橡胶的增塑是指在橡胶中加某些物质，可以使得橡胶分子间的作用力降低，从而降低橡胶的玻璃化温度，令橡胶可塑性、流动性，便于压延、压出等成型操作，同时还能改善硫化胶的某些物理机械性能。现有的橡胶的耐热性比较差，不适用于高温环境。
技术实现思路
本专利技术的目的是针对上述存在的问题提供一种耐高温橡胶增塑材料及其制备方法，添加到橡胶中能起到耐热的效果。上述的目的通过以下技术方案实现：耐高温橡胶增塑材料，由以下重量份数的物质组成：耐高温橡胶增塑材料，由以下重量份数的物质组成：耐高温橡胶增塑材料，由以下重量份数的物质组成：上述耐高温橡胶增塑材料的制备方法，该方法为，按照上述重量比取三甘油酯；二甲基甲酰胺；己二酸二辛酯；抗氧剂，加入到反应釜中，进行聚酯化反应，再经减压蒸馏即可。有益效果：本专利技术生产的耐高温橡胶增塑材料拥有优异的耐热性、耐老化性、耐油、耐溶剂性能、耐腐蚀、本文档来自技高网...

【技术保护点】
1.一种耐高温橡胶增塑材料，其特征是：由以下重量份数的物质组成：

【技术特征摘要】
1.一种耐高温橡胶增塑材料，其特征是：由以下重量份数的物质组成：2.根据权利要求1耐高温橡胶增塑材料，其特征是：由以下重量份数的物质组成：3.根据权利要求1耐高温橡胶增塑材料，其特征是：由以...