The invention relates to an ultra-high performance concrete composition with self-leveling and low self-shrinkage, whose raw material components include powder material, quartz sand and water reducing agent, and the powder materials include cement 20-30%, ore powder 15-20%, heavy calcium powder 1-8%, rheological regulator 1-7%, glass beads 1-3% in proportion to the raw material components. By weight percentage, the quartz sands include: 0.4mm < particle size < 0.8mm quartz sands 5-15%, 0.3mm < particle size < 0.4mm quartz sands 20-25%, 0.075mm < particle size < 0.3mm quartz sands 10-20%. The ultra-high performance concrete composition has good fluidity, self-leveling, long fluidity retention time, proper paste operation time, small self-shrinkage value, and better durability and strength.
【技术实现步骤摘要】
自流平低自收缩的超高性能混凝土组合物
本专利技术涉及混凝土
，特别是涉及一种自流平低自收缩的超高性能混凝土组合物。
技术介绍
超高性能混凝土(UHPC)是一种新兴的水泥基复合材料，具备超高强度、高耐久性、低孔隙率的特点。其抗压强度通常可以达到120MPa以上。目前，UHPC已逐步应用于桥梁、建筑外立面构件、以及各类装饰构件中。UHPC所用材料与普通材料不同，其传统的组成材料包括以下几种：(1)水泥；(2)具有良好级配的细砂；(3)磨细石英砂粉；(4)硅灰、偏高岭土等矿物掺合料；(5)高性能减水剂；(6)纤维。随着UHPC材料的发展，市面上已有部分产品销售，但仍存在如下问题：(1)UHPC之所以具备超高强度和高耐久性，是因其水胶比远低于普通混凝土，通常为0.13～0.20，因此导致浆体粘度高、流动性差，且表面失水较快，易结皮，浆体流动性损失快。(2)由于UHPC具备较低的水胶比，且配方中胶凝材料的比例通常较高，即拥有较高的胶骨比，加之UHPC通常会掺入部分超细掺合料(如硅灰等)，从而导致配方的自收缩较大。一方面，自收缩较大会导致构件早期应力集中，从而在后期容易...
【技术保护点】
1.一种自流平低自收缩的超高性能混凝土组合物，其特征在于，其原料组分包括粉体材料、石英砂和减水剂；以占所述原料组分的重量百分比计，所述粉体材料包括：
【技术特征摘要】
1.一种自流平低自收缩的超高性能混凝土组合物，其特征在于，其原料组分包括粉体材料、石英砂和减水剂；以占所述原料组分的重量百分比计，所述粉体材料包括：以占所述原料组分的重量百分比计，所述石英砂包括：0.4mm≤粒径≤0.8mm石英砂5～15％0.3mm＜粒径＜0.4mm石英砂20～25％0.075mm≤粒径≤0.3mm石英砂10～20％；所述减水剂的用量为所述粉体材料总重量的0.6～1％。2.根据权利要求1所述的超高性能混凝土组合物，其特征在于，以占所述原料组分的重量百分比计，所述粉体材料包括：以占所述原料组分的重量百分比计，所述石英砂包括：0.4mm≤粒径≤0.8mm石英砂9～12％0.3mm＜粒径＜0.4mm石英砂22～23％0.075mm≤粒径≤0.3mm石英砂14～15％；所述减水剂的用量为所述粉体材料总重量的0.7～0.9％。3.根据权利要求1所述的超高性能混凝土组合物，其特征在于，所述重钙粉为超细重钙粉，D50＝2～5μm。4.根据权利要求1所述的超高性能混凝土组合物，其特征在于，所述水泥的D50＝18～22μm；所述矿粉的D50＝10～15μm；所述流变调节剂的D50＝1～...
【专利技术属性】
技术研发人员：马磊，张新星，林豪，田冠飞，
申请(专利权)人：华润水泥技术研发有限公司，
类型：发明