The invention discloses a steel slag composite modifier for grinding and oil absorption and its preparation method, which comprises ethylene glycol 1.0%~2.0%, triethanolamine 1.0%~2.0%, silane coupling agent 4.0%~8.0%, oxalic acid 1.0%~8.0%, anhydrous ethanol 85.5%~92.5%, ethylene glycol triethanolamine mixture is obtained by stirring 50~100 minutes with 400~800r/min at 20~35 ~C. The silane coupling agent and oxalic acid mixture were obtained by mixing the mixture of silane coupling agent and oxalic acid at the speed of 600-1200 r/min and 60-120 min at the temperature of 20-35 (?) and mixing them at the speed of 500-1000 r/min for 10-20 min at the temperature of 20-35 (?). The problem of poor grindability and compatibility of existing steel slag was solved, and the ultra-fine powdering and oil absorption value of steel slag was increased, so as to realize the high value-added application of steel slag.
【技术实现步骤摘要】
一种助磨-吸油的钢渣复合改性剂及其制备方法
本专利技术属于钢渣改性剂领域，具体涉及一种助磨-吸油的钢渣复合改性剂及其制备方法。
技术介绍
钢渣是炼钢过程中产生的固体废弃物，约占炼钢产量的15％～20％。钢渣主要的矿物相为硅酸三钙、硅酸二钙、钙镁橄榄石、铁铝酸钙以及硅、镁、铁、锰、磷的氧化物形成的固熔体，还含有少量游离氧化钙以及金属铁等。上述矿物相的存在导致钢渣易磨性差且相容性差，极大地限制了钢渣应用，导致大量钢渣堆存，不仅占用空间，而且还对周围环境和地下水造成污染，如何改性钢渣性质，提高钢渣利用规模，是迫切需要解决的问题。目前，利用表面改性技术实现钢渣的性质改变是钢渣利用的主要研究方向，尤其是改善现有技术中钢渣易磨性差且相容性差的问题。面对上述问题，利用材料复合方法制备具有助磨-吸油性能的钢渣复合改性剂，提高钢渣的超微粉化和钢渣的吸油值，实现钢渣的高附加值应用，促进钢铁企业增效。
技术实现思路
为了解决现有钢渣易磨性差且相容性差的问题，本专利技术提供了一种助磨-吸油的钢渣复合改性剂及其制备方法，利用有机物醇胺、硅烷偶联剂与有机酸进行复合，并且对搅拌温度、搅拌速度和搅拌...
【技术保护点】
1.一种助磨‑吸油的钢渣复合改性剂，其特征在于，按重量百分比计，包括以下组分：
【技术特征摘要】
1.一种助磨-吸油的钢渣复合改性剂，其特征在于，按重量百分比计，包括以下组分：所述乙二醇为分析纯；所述三乙醇胺为分析纯；所述硅烷偶联剂选自工业纯的KH550、KH560和KH570中至少一种；所述草酸为工业纯；所述无水乙醇为分析纯。2.根据权利要求1所述的助磨-吸油的钢渣复合改性剂，其特征在于，按重量百分比计，包括以下组分：所述乙二醇为分析纯；所述三乙醇胺为分析纯；所述硅烷偶联剂为工业纯；所述草酸为工业纯；所述无水乙醇为分析纯。3.根据权利要求1所述的助磨-吸油的钢渣复合改性剂，其特征在于，按重量百分比计，包括以下组分：所述乙二醇为分析纯；所述三乙醇胺为分析纯；所述硅烷偶联剂为工业纯；所述草酸为工业纯；所述无水...
【专利技术属性】
技术研发人员：王林，龙红明，黄华，张浩，
申请(专利权)人：上海宝田新型建材有限公司，安徽工业大学，湛江宝钢新型建材科技有限公司，
类型：发明
国别省市：上海,31