The invention discloses a high strength solid surface adhesive, which comprises A and B agents. The A agent comprises 100 parts of methyl methacrylate, 1 to 20 parts of functional monomers of methacrylic acid, 0.1 to 0.5 parts of n-dodecyl mercaptan, 0.1 to 0.3 parts of azodiisobutyronitrile, 0.5 to 5 parts of thickener, 0.2 to 5 parts of accelerator and the B agent comprises the following weight parts. Dioctyl terephthalate and benzoyl peroxide were 8 9.5 and 0.1 5 parts respectively. The functional monomer of methacrylic acid is introduced into the binder of solid surface material. The functional monomer has the characteristics of improving bending resistance, cohesion and impact resistance, greatly improving the cohesive strength and meeting the requirements of higher construction standards.
【技术实现步骤摘要】
一种高强度实体面材胶粘剂及其制备方法
本专利技术涉及胶黏剂领域，具体是指一种高强度实体面材胶粘剂及其制备方法。
技术介绍
实体面材开发于上世纪九十年代，实体面材胶粘剂是实体面材加工中最重要的辅助材料，胶粘剂的性能决定了实体面材的加工质量。现使用的实体面材胶粘剂为A、B双组份胶，A剂主要以甲基丙烯酸甲酯与聚甲基丙烯酸以按一定比例混合、溶解、加入二氧化硅增稠，并以有机胺作为促进剂，B剂以饱和溶剂溶解过氧化苯甲酰(BPO)，使用时A、B剂按比例混合粘结固化。其缺点是粘结强度差，不足以满足更高施工标准的要求。
技术实现思路
有鉴于此，本专利技术所要解决的技术问题，就是提出一种高强度实体面材胶粘剂及其制备方法，该胶粘剂采用甲基丙烯酸甲酯本体聚合，加入官能团单体与甲基丙烯酸甲酯共聚。官能性单体具有提高耐弯曲性能，粘结性及耐冲击性等特点，对粘结剂的性能有明显提高。为解决上述技术问题，本专利技术采用以下技术方案予以实现：一种高强度实体面材胶粘剂，包括A剂和B剂，其中，所述A剂包括如下重量份的组分：所述B剂包括如下重量份的组分：对苯二甲酸二辛酯8-11.4份；过氧化苯甲酰0.1～5份。...
【技术保护点】
1.一种高强度实体面材胶粘剂，其特征在于，包括A剂和B剂，其中，所述A剂包括如下重量份的组分：
【技术特征摘要】
1.一种高强度实体面材胶粘剂，其特征在于，包括A剂和B剂，其中，所述A剂包括如下重量份的组分：所述B剂包括如下重量份的组分：对苯二甲酸二辛酯8-11.4份；过氧化苯甲酰0.1～5份。2.根据权利要求1所述的高强度实体面材胶粘剂，其特征在于，所述的甲基丙烯酸官能单体为甲基丙烯酸羟乙酯、甲基丙烯酸羟丙酯、甲基丙烯酸缩水甘油酯中的一种或多种。3.根据权利要求1所述的高强度实体面材胶粘剂，其特征在于，所述增稠剂为气相二氧化硅。4.根据权利要求1所述的高强度实体面材胶粘剂，其特征在于，所述的促进剂...
【专利技术属性】
技术研发人员：温占恒，杨代明，王勇刚，
申请(专利权)人：珠海市盛西源机电设备有限公司，
类型：发明
国别省市：广东,44