The invention discloses a wear-resistant Teflon coating, which comprises 30 40 parts of polytetrafluoroethylene resin, 30 35 parts of epoxy resin, 2 5 parts of leveling agent, 0.5 1 part of defoamer, 2 5 parts of pigments, 1 5 parts of modifier, 60 70 parts of solvent according to weight proportion, including 20 30 parts of nano alumina, 10 15 parts of silicon carbide, 1 parts of cerium oxide and oxidation. Twenty-five copies of titanium. The anti-wear Teflon coating prepared by the invention mixes PTFE resin with epoxy resin, has the characteristics of short curing time, high temperature resistance and wear resistance, and adds modifier to improve the wear resistance of the Teflon coating.
【技术实现步骤摘要】
一种耐磨的特氟龙涂料
本专利技术涉及一种涂料领域，特别是一种耐磨的特氟龙涂料。
技术介绍
特氟龙涂料具有小的表面张力，耐油污损、耐腐蚀，使用温度范围广、不粘性突出、热稳定性良好、耐老化性能和抗辐射性能优异等特点，广泛应用于各个行业。但特氟龙涂料耐磨性较差，贮存一段时间后容易分层、絮凝、失效，在一定程度上限制了其应用范围。
技术实现思路
本专利技术的目的是为了解决上述现有技术的不足而提供一种耐磨的特氟龙涂料。为了实现上述目的，本专利技术所设计的一种耐磨的特氟龙涂料，按照重量配比份包括聚四氟乙烯树脂30-40份、环氧树脂30-35份、流平剂2-5份、消泡剂0.5-1份、颜料2-5份、改性剂1-5份、溶剂60-70份；其中改性剂按重量份包括纳米氧化铝20-30份、碳化硅10-15份、氧化铈1-5份以及氧化钛20-25份。所述流平剂为聚丙烯酸含氟酯流平剂；所述消泡剂为有机硅氧烷；所述溶剂为乙醇或者丙醇。所述流平剂为聚丙烯酸含氟酯流平剂，对丙烯酸树脂、聚氨酯、聚酯、环氧树脂，短油度醇酸树脂有优异的流平性；具有用量小、性价比高、效果显著的特点。所述消泡剂为有机硅氧烷，可降低其分子的内摩擦力、应力，从而起流平、消泡的作用，同时具有耐高温，抗静电性及抗污性能的特点。所述颜料包括钛白粉、氧化铁红和酞菁蓝，这可以根据客户的需要来选择。本专利技术得到的一种耐磨的特氟龙涂料，将聚四氟乙烯树脂与环氧树脂混合使用，具有固化时间短、耐高温、耐磨的特点，添加改性剂，提高了特氟龙涂料的耐磨性。具体实施方式下面结合实施例对本专利技术进一步说明。实施例1：本实施例提供的一种耐磨的特氟龙涂料，按照重...
【技术保护点】
1.一种耐磨的特氟龙涂料，其特征在于：按照重量配比份包括聚四氟乙烯树脂30‑40份、环氧树脂30‑35份、流平剂2‑5份、消泡剂0.5‑1份、颜料2‑5份、改性剂1‑5份、溶剂60‑70份；其中改性剂按重量份包括纳米氧化铝20‑30份、碳化硅10‑15份、氧化铈1‑5份以及氧化钛20‑25份。
【技术特征摘要】
1.一种耐磨的特氟龙涂料，其特征在于：按照重量配比份包括聚四氟乙烯树脂30-40份、环氧树脂30-35份、流平剂2-5份、消泡剂0.5-1份、颜料2-5份、改性剂1-5份、溶剂60-70份；其中改性剂按重量份包括纳米...