The present invention provides a production process of fly ash fire retardant coating, which consists of fly ash, expanded vermiculite, perlite, mica, special additive (A), composite modifier (FH), light calcium carbonate, weight ratio: 450 430:115 130:160:140:30 40:3 5:8 12; and process is: fly ash, expanded vermica, special additive (A). Compound modifier (FH) and light calcium carbonate were put into the mixer in order to mix for 20 seconds. The invention has excellent fireproof performance and can be used for a long time in high temperature hydrocarbon fire at 1100 C. The coating has weatherproof, waterproof, non-shrinkage, high strength, flat surface, easy construction and repair, and improves the shortcomings of easy powdering, cracking and falling off of the fireproof coating used outdoors.
【技术实现步骤摘要】
粉煤灰防火涂料生产工艺
本专利技术提供了一种粉煤灰防火涂料生产工艺,以提高防火涂料耐火性能,改善防火涂料的易抹涂性,并增加其抗压强度。属于组合式消防材料技术。
技术介绍
我国防火涂料的发展较国外工业发达国家较晚;但是发展速度较快,按照GB14907-2002《钢结构防火涂料的技术性能》将其分为室内和室外,按其用途可分为厚型、薄型和超薄型。钢结构体系具有强度高、自重轻、性能稳定、韧性好、安装容易、施工周期短、抗震性能好、环境污染少等综合优势。它在民用高层建筑、工业厂房、石油化工、核工业、国防等领域广泛使用。但是钢材常温热导率高达58.2W/(m.K),升温或遇火时热导率会更高,因而传热速度更快。如钢材在20℃时强度450mpa,而到614℃时强度就只有70mpa,几乎失去承载能力,所以在火灾时15min左右,钢材就会如面条一样软下来。钢结构防火涂料的优劣是保护钢结构在火灾中通过阻燃隔热等原理尽量延长钢结构在火灾中达到的临界温度过程的关键。厚型钢结构防火涂料主要成份为:无机材料,其防火性能稳定、耐候性能好,可长期使用。但是由于该材料主要原辅材料多为颗粒较大的无机隔热材料,施工后强度低,表面不平整,影响建筑物的整体美观。粉煤灰是我国当前排量较大的工业废渣之一,其排渣量已达3000万吨,随着电力工业的发展,燃煤电厂的增加其排放量也在逐年增加,如不加以处理,就会产生粉尘污染大气,并有着化学物质还会对人体和生物造成危害。因此粉煤灰的利用已引起人们的广泛关注。但是粉煤灰有其优点,不但颗粒细,而且研究表明:在厚型钢结构防火涂料中掺和,节约了细骨料,减少了用水量,改变了涂料 ...
【技术保护点】
1.一种粉煤灰防火涂料生产工艺,组份为:粉煤灰、膨胀蛭石、珍珠岩、云母、特制添加剂(A)、复合改性剂(FH)、轻质碳酸钙;重量比为:450‑430:115‑130:160‑140:30‑40:3‑5:8‑12;工艺为:将粉煤灰、膨胀蛭石、珍珠岩、云母、特制添加剂(A)、复合改性剂(FH)、轻质碳酸钙按顺序放入搅拌机进行混合搅拌20秒,其特征在于所述防火涂料的组份中设有粉煤灰;所述防火涂料的组份粉煤灰、膨胀蛭石、珍珠岩、云母、特制添加剂(A)、复合改性剂(FH)、轻质碳酸钙的重量比为:450‑430:115‑130:160‑140:30‑40:3‑5:8‑12。
【技术特征摘要】
1.一种粉煤灰防火涂料生产工艺,组份为:粉煤灰、膨胀蛭石、珍珠岩、云母、特制添加剂(A)、复合改性剂(FH)、轻质碳酸钙;重量比为:450-430:115-130:160-140:30-40:3-5:8-12;工艺为:将粉煤灰、膨胀蛭石、珍珠岩、云母、特制添加剂(A)、复合改性剂(...