The invention discloses a high tearing rubber bowl material for a crushing hammer and a preparation method thereof. The rubber bowl material comprises 50 to 200 parts by weight, 2 to 15 parts by activator, 50 to 200 parts by reinforcing filler, 2 to 30 parts by plasticizer, 2 to 20 parts by tear resistance, 1 to 5 parts by fatigue resistance and 1 to 5 parts by vulcanizing agent. The present invention improves the tear resistance and fatigue resistance of rubber bowl material by optimizing the kinds and dosage of activator, reinforcing filler, plasticizer, tear resistance agent, fatigue resistance agent and vulcanizing agent. The tear strength of the material can reach 85KN/m, and the stretching fatigue can reach 2.8 million times. Compared with the existing rubber bowl material, the performance can be improved by 30%-40%.
【技术实现步骤摘要】
一种破碎锤用高撕裂橡胶皮碗材料及其制备方法
本专利技术涉及橡胶
，具体涉及一种破碎锤用高撕裂橡胶皮碗材料及其制备方法。
技术介绍
破碎锤作为挖掘机的重要部件，在矿山开采、冶金、铁路、公路破碎维修、旧建筑拆除中发挥重要作用。破碎锤最重要的特征就是其打击力和冲击能量，所以中大型的破碎锤一般包含“液压+氮气”冲击系统，以增加其打击力。氮气冲击系统主要是靠橡胶皮碗压缩氮气来完成的，而由于破碎锤冲击频率高、压力大，橡胶皮碗在压力下反复压缩、曲挠，橡胶容易自身生热、疲劳，在高温下的反复动作，橡胶极易发生疲劳、老化。一旦皮碗发生破裂，则需要拆除破碎锤。因此橡胶皮碗的更换非常麻烦，维修成本很高。目前行业内橡胶皮碗材料一般以丁腈橡胶为主，也有部分采用氢化丁腈橡胶。丁腈橡胶耐温、拉伸强度、撕裂等性能一般，损坏频率很高；氢化丁腈橡胶使用寿命明显大于前者，但是制造成本远远高于前者，且其性能尚未达到预期。
技术实现思路
本专利技术的目的在于克服现有技术的不足之处而提供一种破碎锤用高撕裂橡胶皮碗材料，该橡胶皮碗材料具有优异的抗撕裂性能和抗疲劳性能。为实现上述目的，本专利技术采取的技术方案如...
【技术保护点】
1.一种破碎锤用高撕裂橡胶皮碗材料，其特征在于，包括以下重量份的组分：
【技术特征摘要】
1.一种破碎锤用高撕裂橡胶皮碗材料，其特征在于，包括以下重量份的组分：2.根据权利要求1所述的破碎锤用高撕裂橡胶皮碗材料，其特征在于，所述活性剂为氧化锌、氧化镁、硬脂酸、聚乙二醇、硬脂酸盐中的至少一种。3.根据权利要求1所述的破碎锤用高撕裂橡胶皮碗材料，其特征在于，所述补强填充剂为矿物填料；优选地，所述补强填充剂包括炭黑、白炭黑、硅藻土、硅酸钙陶土中的至少一种。4.根据权利要求1所述的破碎锤用高撕裂橡胶皮碗材料，其特征在于，所述增塑剂为酯类增塑剂；优选地，所述增塑剂为邻苯二甲酸二辛酯、对苯二甲酸二辛酯、偏苯三酸三辛酯、癸二酸二辛酯、己二酸二辛酯、乙二酸二(丁氧基乙氧基乙)酯中的至少一种。5.根据权利要求1所述的破碎锤用高撕裂橡胶皮碗材料，其特征在于，所述抗撕裂剂包括多壁碳纳米管、由无定形结构和结晶体构成的石油树脂聚合物中的至少一种。6.根据权利要求1所述的破碎锤用高撕裂橡胶皮碗材料，其特征在于，所述抗疲劳剂为甲基柠糠酰亚胺、活化型酚醛树脂和间甲白体系组成的络合物，所述抗疲劳剂的制备方法如下：将脂肪酸锌、芳香羧酸锌、补强增硬树脂和增粘树脂混合，在130-150℃熔融，然后加入1,3-双(柠糠酰...
【专利技术属性】
技术研发人员：杨文良，张文瑞，胡维科，
申请(专利权)人：广州弗西林橡塑有限公司，
类型：发明
国别省市：广东,44