The invention discloses a preparation method of functionalized organic magnesium salts. The organic acid is completely dissolved in distilled water to form an organic acid aqueous solution, and then inorganic magnesium salts are added to the organic acid aqueous solution. The inorganic magnesium salts are magnetic stirred for 1 to 5 hours at 70-100 (?) C to remove distilled water and dry in vacuum. The white powder solid obtained is functionalized organic magnesium salts. The intrinsic flame-retardant polyester (PET) composites prepared with functionalized organic magnesium salts as flame retardants not only solve the compatibility between inorganic particles and matrix, but also solve the problem of poor flame-retardant performance of polyester (PET) plastics in the existing production process.
【技术实现步骤摘要】
一种功能化有机镁盐的制备及在制备聚酯复合材料中的应用
本专利技术涉及一种功能化有机镁盐的制备方法，本专利技术同时涉及以功能化有机镁盐为阻燃剂制备阻燃型聚酯（PET）复合材料的应用，属于阻燃材料
和高分子材料合成
技术介绍
早期合成的聚酯大多为脂肪族聚酯产品，分子量与熔点都比较低并且极易溶于水，直到1941年英国人J.R.Whenfield和J.T.Dikson使用对苯二甲酸与乙二醇为原料，合成出比脂肪族聚酯熔点高的聚对苯二甲酸乙二醇酯。聚酯（PET）属于线型热塑性材料，由于其具有优良的力学性能、热性能，且成本较低已广泛应用于纤维、工程塑料、薄膜包装等诸多领域。尤其是以PET为原料生产的涤纶是我国合成纤维中产量最大的品种。但是传统的聚酯PET具有可燃性，燃烧速度快，不宜熄灭，而且在燃烧过程中产生的熔融滴落物还可以引燃其他的物质，从而加剧了材料的燃烧，由此造成了严重的火灾和人员伤亡事故。因此预防火灾是目前社会重点研究的主题。为了提高合成材料的安全性，通过在合成高分子材料中加入合适的阻燃剂，可以使合成材料达到阻燃、抑烟的目的。目前用于聚酯阻燃改性的阻燃剂...
【技术保护点】
1.一种功能化有机镁盐的制备方法，是将有机酸完全溶解在蒸馏水中形成有机酸水溶液，再向其中加入无机镁盐，在70~100℃下磁力搅拌1~5h，去除蒸馏水，真空干燥，所得白色粉末状固体即为功能化有机镁盐。
【技术特征摘要】
1.一种功能化有机镁盐的制备方法，是将有机酸完全溶解在蒸馏水中形成有机酸水溶液，再向其中加入无机镁盐，在70~100℃下磁力搅拌1~5h，去除蒸馏水，真空干燥，所得白色粉末状固体即为功能化有机镁盐。2.如权利要求1所述一种功能化有机镁盐的制备方法，其特征在于：有机酸为亚磷酸、丁二酸、对氨基苯甲酸、庚二酸中的至少一种。3.如权利要求1所述一种功能化有机镁盐的制备方法，其特征在于：无机镁盐为氢氧化镁、碳酸镁，硼酸镁，氧化镁。4.如权利要求3所述一种功能化有机镁盐的制备方法，其特征在于：无机镁盐的粒径为400~600nm。5.如权利要求1~4所述任何一种功能化有机镁盐的制备方法，其特征在于：有机酸与无机微粒的摩尔比为0.5:1~3:1。6.如权利要求1所述方法制备的功能化有机镁盐用于聚酯复合材料的制备。7.如权利要求1所述功能化有机镁盐用于聚酯复合材料的制备，其特征在于：将对苯二甲酸...
【专利技术属性】
技术研发人员：雷自强，和瑾楠，杨尧霞，杨志旺，曾巍，石剑平，
申请(专利权)人：西北师范大学，
类型：发明
国别省市：甘肃,62