The invention provides an environment-friendly, non-toxic, rapid reaction and low water absorption polyurethane elastomer composition, in which the prepolymer obtained by the reaction of vegetable oil polyols with polyisocyanate is one component, and the mixture of vegetable oil polyols, chain extenders, color pastes and various functional auxiliaries is another component. The spraying rapid solidification method is adopted to achieve the purpose of simple construction and improve construction efficiency. The products obtained have high strength, low water absorption, safety and environmental protection, and are suitable for large-scale construction of lining of drinking water pipelines and tanks.
【技术实现步骤摘要】
一种饮用水容器用快速喷涂改性聚氨酯涂层材料及其制备方法
本专利技术属于聚氨酯弹性体涂层及其制备方法，具体涉及一种饮用水容器用快速喷涂改性聚氨酯涂层材料及其制备方法。
技术介绍
随着生活水平的日益提高和保健意识的增强，人们对直接影响人类健康的饮用水接触涂层的要求也越来越高。随着新型材料的应用，目前可应用于饮用水接触涂层的材质品种非常繁多。从材质上主要有金属材质、非金属材质，从成品来分主要是容器和管道，大口径管道主要包括钢管、球墨铸铁管，中小口径的管材常用薄壁不锈钢、聚乙烯管等。钢管和球墨铸铁管若不进行任何处理会很容易产生腐蚀。管道腐蚀后不仅降低了输水能力、增加的电耗，主要的是对供水水质产生了严重的影响，对饮用者的健康产生威胁。因此钢管和铸铁管必须内衬涂防腐涂层才能应用于供水管道中。现有的内衬主要有水泥砂浆衬里、环氧树脂、聚氨酯涂层、PE膜涂层等产品。传统的水泥砂浆衬里易开裂，且涂层较厚，大大降低了输送效率，且衬里呈碱性，与水接触后会增大水中的pH值，对水质有碱性劣化现象。环氧树脂固化慢，且温度对其固化速度有很大的影响，冬天、寒冷地区无法正常施工，涂装后需要几天时间才...
【技术保护点】
1.饮用水容器用快速喷涂改性聚氨酯涂层材料，其特征在于两种组分构成组合物：A组分：异氰酸酯封端预聚体的合成及B组分植物油聚醚多元醇、扩链剂、颜料、助剂的混合。
【技术特征摘要】
1.饮用水容器用快速喷涂改性聚氨酯涂层材料，其特征在于两种组分构成组合物：A组分：异氰酸酯封端预聚体的合成及B组分植物油聚醚多元醇、扩链剂、颜料、助剂的混合。2.根据权利1所述的A组分异氰酸酯封端预聚体的合成方法：以重量份计，将55-85份的多异氰酸酯加入到有氮气保护的反应釜中，匀速搅拌，加热至50～60℃，向反应釜中缓慢加入15-50份的植物油聚醚多元醇，在60～90℃下，保温反应0.5-1.5h小时，加入0.1-1份的催化剂，继续在此温度搅拌反应1.5-2.5h后冷却出料。3.根据权利1所述B组分的制备方法是：以重量份计，25-75份的植物油多元醇、15-30份扩链剂、5-10份的色浆、5-15份助剂常温混合，利用高剪切分散设备高速搅拌20～40分钟后出料。4.根据权利1所述组合物，其特征在于：所述A组分与B组分的当量比，也就是异氰酸酯指数在0.9-1.2之间进行配合，所述A组分与所述B组分按体积比1∶1配合。5.根据权利1-4任意项所述组合物，其特征在于：所述A组分中的多异氰酸酯为官能度在2.0～2.7之间，2，4’-二苯基甲烷二异氰酸酯，4，4’-二苯基甲烷二异氰酸酯，碳化二亚胺-脲酮亚胺改性的4，4’-二苯基甲烷二异氰酸酯、2，4’-二苯基甲烷二异氰酸酯，多次甲基多苯基异氰酸...
【专利技术属性】
技术研发人员：亓峰，任衍麟，王宝利，姜深生，
申请(专利权)人：青岛格林沃德新材料科技有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。