The invention relates to a transparent geopolymer and a preparation method thereof. The light-transmitting geopolymer is composed of geopolymer and light-transmitting elements. The mass fractions of the said geopolymer are: metakaolin 50 100, fly ash 10 50, red mud 10 50, titanium tailings 5 20, zeolite powder 5 15, caustic alkali 10 20, water glass 25 40, vegetable oil 0.1 1 and defoamer 0.1 0.5; The main component of the light-transmitting element is methyl. Acrylic acid methyl ester or acrylic acrylic acrylic acrylic bar; the ratio of the total area of the light transmission element to the cross section area of the geopolymer is 0.1 0.5. The transparent geopolymer provided by the invention has good transparency, simple preparation method, and most raw materials come from industrial waste, which is economical and environmental protection.
【技术实现步骤摘要】
一种透光地聚合物及其制备方法
本专利技术涉及建筑材料
，特别涉及一种透光地聚合物及其制备方法。技术背景透光水泥是匈牙利建筑师AronLosonczj于2002年首先专利技术，此后在美国、法国等国家被应用。用透光水泥可制成园林建筑制品、装饰板材、装饰砌块和曲面波浪型，为建筑师的艺术想象与创作提供了实现的可能性。透光水泥是一种全新透光材料，在材料组成、透光原理、材料性能等各个方面与传统的透光材料完全不同。其材料基本组成是大量的光纤以一定空间排列组合方式埋入水泥基材料中。然而，光纤主要是成分为SiO2，其虽具有优异的导光性能，但高碱性的硅酸盐水泥对光纤维具有强烈侵蚀作用，降低透光性能及透光建筑物的耐久性。因此，未来透光混凝土中的导光材料必将朝着多元化发展，透光材料的高韧性，低脆性，高透光性，低成本化成为其主要的研究趋势。地聚合物是由硅氧与铝氧四面体组成的，具有空间三维网络状键接结构的新型无机硅铝质胶凝材料。与传统水泥相比，地聚合物的原材料来源广泛，工业废气物粉煤灰、赤泥，天然煅烧高岭土均可以作为原材料。此外其生产能耗低、CO2排放量小，具有快硬，高韧性。此外，...
【技术保护点】
1.一种透光地聚合物，其特征在于，各原材料的组份数为：偏高岭土50‑100份；粉煤灰10‑50份；赤泥10‑50份；提钛尾渣5‑20份；沸石粉5‑15份；苛性碱10‑20份；水玻璃25‑40份；植物油0.1‑1份；消泡剂0.1‑0.5份；透光元件。
【技术特征摘要】
1.一种透光地聚合物，其特征在于，各原材料的组份数为：偏高岭土50-100份；粉煤灰10-50份；赤泥10-50份；提钛尾渣5-20份；沸石粉5-15份；苛性碱10-20份；水玻璃25-40份；植物油0.1-1份；消泡剂0.1-0.5份；透光元件。2.权利要求1所述的透光地聚合物，其特征在于，是由以下步骤制备得到的：1)利用偶联剂对透光元件的表面进行处理，将透光元件固定在模具底部，透光元件之间的距离为3mm-4mm；2)将水玻璃放置与冷水浴中，加入固体苛性碱，缓慢搅拌直达苛性碱完全溶解，密封放置24h，作为碱激发剂；3)将植物油与消泡剂加入适量的水中，制备为外加剂溶液；4)将步骤2)制备的碱激发剂与步骤3)制备的外加剂溶液依次加入胶凝材料中，搅拌3min，然后依次加入矿物掺和料，继续搅拌3min，使地聚合物浆体均匀混合；5)将步骤4)制备的地聚合物浆...
【专利技术属性】
技术研发人员：彭小芹，孙科科，王淑萍，曾路，胡婷婷，姬广祥，
申请(专利权)人：重庆大学，
类型：发明
国别省市：重庆,50