A Water Absorbing Ink Canvas and Its Manufacturing Method

The invention discloses a preparation method of a water-absorbing ink canvas, which comprises a base material, an isolation layer, a coating and an ink-absorbing layer from bottom to top. The separating layer, coating layer and ink absorbing layer are stirred separately and coated on the base material for drying. This application uses propylene as isolation layer to prevent paint from penetrating into water-absorbing ink canvas. The setting of coating and ink-absorbing layer can make water-absorbing ink canvas absorb water and ink better, broaden the painting tools of Chinese painting, improve the anti-aging function of water-absorbing ink canvas, and do not fade.

【技术实现步骤摘要】
一种吸水墨画布及其制作方法
本专利技术涉及吸水墨画布
，具体涉及一种吸水墨画布及其制作方法。
技术介绍
中国传统的绘画是在宣纸上进行的这就限制了中国画的发展，为了更好的发展中国画，需要对现有的绘画载体进行改进，使中国画以更多的形式出现在大众眼前。画布作为一种绘画载体，在使用的过程中存在这一些问题，例如吸水性差、易发黄、容易皱、不容易保存、也不适合室外悬挂、被雨淋到会使画褪色等。
技术实现思路
本专利技术的目的是提供一种吸水墨画布及其制备方法，解决吸画布吸水性差、不容易吸墨的问题。为了解决上述问题，本专利技术采用如下技术方案：一种吸水墨画布，所述吸水墨画布从下到上依次为基材、隔离层、涂层和吸墨层。优选的，所述基材为棉麻织物。优选的，所述隔离层为丙烯液体5～10份。优选的，所述涂层按照重量份包括：去离子水10～30份，聚乙烯醇3～5份，钛白粉8～10份，碳酸氢钙3～5份，粘合剂1～3份。优选的，所述吸墨层按照重量份包括：去离子水20～40份，聚乙烯醇2～3份，纳米二氧化硅8～12份，固色剂6～8份，助剂3～4份。进一步优选的，所述助剂为15％的分散剂、10％的消泡剂、10％的防腐剂和6本文档来自技高网...

【技术保护点】
1.一种吸水墨画布，其特征在于，所述吸水墨画布从下到上依次为基材、隔离层、涂层和吸墨层。

【技术特征摘要】
1.一种吸水墨画布，其特征在于，所述吸水墨画布从下到上依次为基材、隔离层、涂层和吸墨层。2.根据权利要求1所述的吸水墨画布，其特征在于，所述基材为棉麻织物。3.根据权利要求1所述的吸水墨画布，其特征在于，所述隔离层为丙烯液体5～10份。4.根据权利要求1所述的吸水墨画布，其特征在于，所述涂层按照重量份包括：去离子水10～30份，聚乙烯醇3～5份，钛白粉8～10份，碳酸氢钙3～5份，粘合剂1～3份。5.根据权利要求1所述的吸水墨画布，其特征在于，所述吸墨层按照重量份包括：去离子水20～40份，聚乙烯醇2～3份，纳米二氧化硅8～12份，固色剂6～8份，助剂3～4份。6.根据权利要求5所述的吸水...

【专利技术属性】
技术研发人员：宋兆峰，王默，宿晓雨，肖航，王燕，兰海涛，颜宇萌，张哲，张雷，
申请(专利权)人：宋兆峰，
类型：发明
国别省市：河北,13