The invention provides a welding method of one-sided welding and two-sided forming of CO2 ceramic liner. The welding method of the invention can form beautiful welds in actual welding. Compared with the argon arc welding in the prior art, the welding method of the invention has high welding quality. With the help of the ceramic liner on the back of the weld, the high temperature resistance of the liner is used as the basis for the back weld forming. To achieve single-side welding and double-side forming, the welding stability of base metal is high. The most important thing is to greatly improve the welding speed, high welding efficiency, and solve the practical problems of slow welding speed and low efficiency existing in the current technology of gas shielded welding.
【技术实现步骤摘要】
一种CO2陶质衬垫单面焊双面成型的焊接方法
本专利技术涉及到气体保护焊
，特别涉及到一种CO2陶质衬垫单面焊双面成型的焊接方法。
技术介绍
气体保护焊是利用气体作为电弧介质并保护电弧和焊接区的电弧焊称为气体保护电弧焊，简称气体保护焊，气体保护焊与其它焊接方法相比，气体保护焊的电弧和熔池的可见性好，焊接过程中可根据熔池情况调节焊接参数，焊接过程操作方便，没有熔渣或很少有熔渣，焊后基本上不需清渣，电弧在保护气流的压缩下热量集中，焊接速度较快，熔池较小，热影响区窄，焊件焊后变形小，有利于焊接过程的机械化和自动化，特别是空间位置的机械化焊接，也可以焊接化学活泼性强和易形成高熔点氧化膜的镁、铝、钦及其合金。不同保护焊工艺面临不同的焊接材料，受到的因素多种多样，因此实际中的焊接速度和效率不一，如气体保护焊中的氩弧焊工艺，具有上述的所述焊接性能，面临不同材料能够在较低的焊接规格电压值下工作，节省焊接成本，但其焊接效率低下，比如焊接母材为Q345R时，采用氩弧焊的焊接工艺能够达到的焊接速度仅为10~15cm/min，这在实际焊接工程施工时，焊接效率低下显示凸出，延误施工进度...
【技术保护点】
1.一种CO2陶质衬垫单面焊双面成型的焊接方法，具体步骤如下：S1.组装焊接坡口，首先将待焊接的母材按需要的坡口形状组装好并固定，然后将陶瓷衬垫粘贴在坡口背面；S2.坡口表面清理；S3.打底焊，采用CO2气体保护焊对坡口处的焊缝进行首层打底焊焊接，焊接间距根据实际坡口大小调整；S4.焊接完毕，拆除焊缝背面的陶质衬垫，检修；S5.焊缝清理。
【技术特征摘要】
1.一种CO2陶质衬垫单面焊双面成型的焊接方法，具体步骤如下：S1.组装焊接坡口，首先将待焊接的母材按需要的坡口形状组装好并固定，然后将陶瓷衬垫粘贴在坡口背面；S2.坡口表面清理；S3.打底焊，采用CO2气体保护焊对坡口处的焊缝进行首层打底焊焊接，焊接间距根据实际坡口大小调整；S4.焊接完毕，拆除焊缝背面的陶质衬垫，检修；S5.焊缝清理。2.根据权利要求1所述一种CO2陶质衬垫单面焊双面成型的焊接方法，其特征在于：在步骤S3与S4之间还包括...
【专利技术属性】
技术研发人员：夏晓松，
申请(专利权)人：重庆欣雨压力容器制造有限责任公司，
类型：发明
国别省市：重庆,50