The invention discloses a preparation method and application of an isomerization catalyst, in order to solve the problem of low yield of the target product due to the existence of isomers in the production process of such compounds. The precursor of the catalyst is composed of a composite oxide or a certain amount of metal salts impregnated with the prepared oxide. The catalyst precursor is calcined at 350-450 degrees C, pressed and formed, and fluorinated at 200-400 degrees C by HF to prepare the fluorinated catalyst. The catalyst is mainly suitable for cis-trans isomerization of hydrofluoroolefins or hydrofluorochloroolefins.
【技术实现步骤摘要】
一种含氟烯烃顺反异构化催化剂的制备方法和用途
本专利技术涉及到一种含氟烯烃顺反异构化催化剂的制备方法和用途，尤其是涉及用于氢氟烯烃或氢氟氯烯烃的顺反异构化反应。
技术介绍
许多含氟烯烃能够基于双键周围取代基的排列而以顺/反异构体形式存在，如1-氟丙烯(CH3CH＝CHF)、1,2-二氟丙烯(HFC＝CFCH3)、1,3-二氟丙烯(CHF＝CHCH2F)、1,2,3-三氟丙烯(CHF＝CFCH2F)、1,3,3-三氟丙烯(CHF＝CHCF2H)、1,3,3,3-四氟丙烯(CHF＝CHCF3)、1,2,3,3-四氟丙烯(HFC＝CFCF2H)、1,2,3,3,3-五氟丙烯(CHF＝CFCF3)等。相应的反式和顺式异构体通常具有不同的物理或化学性质，因此也就产生了不同的应用。如1,3,3,3-四氟丙烯，臭氧损耗潜值为0，温室效应潜值为6，其反式异构体沸点-19℃，可用作制冷剂、发泡剂、气溶胶喷射剂等；反式-1-氯-3,3,3-三氟丙烯，臭氧消耗潜值(ODP)接近于0，温室效应潜值(GWP)为7.0，环保性能优良，已被国际社会认定为第四代氟代烃发泡剂。但该类化合物在制备过...
【技术保护点】
1.一种用于含氟烯烃顺反异构化催化剂的制备方法，其特征在于，该催化剂由催化剂前驱体经350℃～450℃焙烧后，打片压制成型，200℃～400℃HF氟化处理后制得所述的异构化催化剂；所述的催化剂前驱体由复合氧化物或者复合氧化物浸渍的金属盐组成；所述的复合氧化物的金属离子由Fe、Co、Ni中的一种或几种与Mg、Ca中的一种或几种组成；所述的浸渍金属盐为Al、Cr和Zn可溶性盐溶液中的一种或几种的混合物，浸渍量分别为复合氧化物质量的1～10％。
【技术特征摘要】
1.一种用于含氟烯烃顺反异构化催化剂的制备方法，其特征在于，该催化剂由催化剂前驱体经350℃～450℃焙烧后，打片压制成型，200℃～400℃HF氟化处理后制得所述的异构化催化剂；所述的催化剂前驱体由复合氧化物或者复合氧化物浸渍的金属盐组成；所述的复合氧化物的金属离子由Fe、Co、Ni中的一种或几种与Mg、Ca中的一种或几种组成；所述的浸渍金属盐为Al、Cr和Zn可溶性盐溶液中的一种或几种的混合物，浸渍量分别为复合氧化物质量的1～10％。2.如权利要求1所述的一种用于含氟烯烃顺反异构化催化剂的制备方法，所述的复合氧化物的制备方法，其特征在于，将Fe、Co、Ni的可溶性盐的一种或几种与Mg、Ca中的一种或几种的可溶性盐溶于水或者有机溶剂中配制成混合溶液，加热至40℃，向其中加入沉淀剂，调节PH值在8.5～9.5之间，老化1～2h，升高温度至90℃，继续老化8～12h，过滤，将所得沉淀产物洗涤至中性，在120℃下干燥，得到的固体在450～500℃下焙烧4～6h，制得所述的复合氧化物；其中F...
【专利技术属性】
技术研发人员：秦越，吕剑，王博，寇联岗，毛伟，马辉，涂东怀，韩升，赵波，
申请(专利权)人：西安近代化学研究所，
类型：发明
国别省市：陕西,61