The invention provides a heat-resistant nano conductive coating, which is calculated according to the weight fraction, including the following components: 45~65 parts of acrylic emulsion, 15~20 parts of heat resistant polyethylene, 5~10 parts of carbon nano fiber, 1~4 parts of polypyrrole, 3~8 parts of modified nano Zinc Oxide, 2~6 parts of film forming AIDS, 0.1 to 0.5 parts of silicone oil and 30~40 parts of water, and the modified nano Zinc Oxide is mainly composed of zinc acetate and three chlorination. The mass ratio of zinc acetate, silver nitrate and iron trichloride is 6-7:3-6:2-4. The polypyrrole and the nano-carbon fibers need to be added to 2-5 wt% zinc castor oil acid solution for immersion pretreatment. The heat-resistant nano-conductive coating has good conductivity and heat resistance.
【技术实现步骤摘要】
耐热型纳米导电涂料
本专利技术属于纳米材料
，具体涉及一种耐热型纳米导电涂料。
技术介绍
导电涂料是伴随现代科学技术而迅速发展起来的特种功能涂料，至今约有半个世纪的发展历史，美国在1948年公布了将银和环氧树脂制成导电胶的专利，这是最早公开的导电涂料。我国也在20世纪50年代开始研究和应用导电涂料，近年来，导电涂料已在电子、电器、航空、化工、印刷等多种军、民用工业领域中得到应用；与此相应，导电涂料的理论研究也得到了迅速发展，并促进了应用技术的日益成熟与完善。导电涂料按组成和导电机理的不同可以分为结构型(本征型)和添加型(复合型)两种。结构型(本征型)导电涂料是利用自身或经过掺杂之后具有导电功能的高分子材料直接成膜或与其它有机高分子混合；添加型(复合型)导电涂料是通过将导电的无机粒子或有机抗静电剂加入非导电的树脂中，利用树脂的物理机械性能和填料的导电能力而制备导电涂层。添加型导电涂料中导电添加剂主要涉及导电云母、导电炭黑、导电石墨、导电ATO、碳纳米管等；结构型导电涂料中导电聚合物只涉及聚三乙醇胺和改性聚(3,4-乙烯二氧噻吩)-聚苯乙烯磺酸。而碳系填料虽然由...
【技术保护点】
1.一种耐热型纳米导电涂料，其特征在于，按照重量份数计算，包括以下组分：丙烯酸乳液45～65份、耐热聚乙烯15～20份、纳米碳纤维5～10份、聚吡咯1～4份、改性纳米氧化锌3～8份、成膜助剂2～6份、硅油0.1～0.5份及水30～40份；所述改性纳米氧化锌主要由乙酸锌、三氯化铁与硝酸银制备得到，所述乙酸锌、硝酸银与三氯化铁的质量之比为7～9:5～8:1～3；所述聚吡咯与所述纳米碳纤维需要加入到2～5wt％的蓖麻油酸锌溶液进行浸泡预处理。
【技术特征摘要】
1.一种耐热型纳米导电涂料，其特征在于，按照重量份数计算，包括以下组分：丙烯酸乳液45～65份、耐热聚乙烯15～20份、纳米碳纤维5～10份、聚吡咯1～4份、改性纳米氧化锌3～8份、成膜助剂2～6份、硅油0.1～0.5份及水30～40份；所述改性纳米氧化锌主要由乙酸锌、三氯化铁与硝酸银制备得到，所述乙酸锌、硝酸银与三氯化铁的质量之比为7～9:5～8:1～3；所述聚吡咯与所述纳米碳纤维需要加入到2～5wt％的蓖麻油酸锌溶液进行浸泡预处理。2.根据权利要求1所述的耐热型纳米导电涂料，其特征在于，所述改性纳米氧化锌的制备方法包括以下步骤：1)将乙酸锌、三氯化铁与硝酸银加入到丙三醇进行混合，然后超声搅拌30～40分钟，得到分散液；2)向分散液中加入亚麻籽亚油酸和三乙醇胺，超声搅拌混合均匀，得到...
【专利技术属性】
技术研发人员：历建双，历彦程，
申请(专利权)人：安徽吉露科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。