The invention relates to an anti-oxidation electric meter box insulation coating and a preparation method thereof, belonging to the technical field of coatings for electrical products. The anti-oxidation electric meter box insulation coating comprises the following raw materials: 25 35 parts of organic fluorine epoxy resin, 30 45 parts of acrylic resin, 10 18 parts of polysiloxane, 3 10 parts of diphenyl polysiloxane, 15 20 parts of fatty acid polyethylene glycol ester, 1 2 parts of isobutyl nipagin, 5 10 parts of inorganic filler, 1 5 parts of processing aids, 2 3 parts of film-forming agent. The antioxidant electric meter box insulation coating has simple formula and scientific design, excellent corrosion resistance and rust resistance, and provides a simple and practical preparation method of the antioxidant electric meter box insulation coating.
【技术实现步骤摘要】
抗氧化电表箱体绝缘涂料及其制备方法
本专利技术涉及一种抗氧化电表箱体绝缘涂料及其制备方法，属于电工产品用涂料
技术介绍
电表箱的使用环境比较恶劣，需要电表箱具有一定的防腐和防锈性能。目前，一般采用一些适当的表面处理办法，如在表面涂布一层绝缘涂料进行表面改性，但现有的绝缘涂料耐老化、抗氧化性能较差，涂覆后电表箱的使用寿命有限，为了降低成本，提高电表箱的使用率，提高安全系数，急需要对电表箱的表面处理技术进行改进。
技术实现思路
本专利技术的目的是提供一种抗氧化电表箱体绝缘涂料，其配方简单、设计科学，具有优异的防腐性和防锈性；同时本专利技术提供了一种简单实用的抗氧化电表箱体绝缘涂料的制备方法。所述抗氧化电表箱体绝缘涂料，包括以下重量份数的原料：有机氟环氧树脂25-35份，丙烯酸树脂30-45份，聚硅醚10-18份，二苯基聚硅氧烷3-10份，脂肪酸聚乙二醇酯15-20份，尼泊金异丁酯1-2份，无机填料5-10份，加工助剂1-5份，成膜剂2-3份。所述丙烯酸树脂为水分散性丙烯酸树脂。水分散性丙烯酸树脂水分散体的平均粒径为0.5-0.7μm。水分散性丙烯酸树脂为市售产品...
【技术保护点】
1.一种抗氧化电表箱体绝缘涂料，其特征在于包括以下重量份数的原料：有机氟环氧树脂25‑35份，丙烯酸树脂30‑45份，聚硅醚10‑18份，二苯基聚硅氧烷3‑10份，脂肪酸聚乙二醇酯15‑20份，尼泊金异丁酯1‑2份，无机填料5‑10份，加工助剂1‑5份，成膜剂2‑3份。
【技术特征摘要】
1.一种抗氧化电表箱体绝缘涂料，其特征在于包括以下重量份数的原料：有机氟环氧树脂25-35份，丙烯酸树脂30-45份，聚硅醚10-18份，二苯基聚硅氧烷3-10份，脂肪酸聚乙二醇酯15-20份，尼泊金异丁酯1-2份，无机填料5-10份，加工助剂1-5份，成膜剂2-3份。2.根据权利要求1所述的抗氧化电表箱体绝缘涂料，其特征在于：丙烯酸树脂为水分散性丙烯酸树脂。3.根据权利要求1所述的抗氧化电表箱体绝缘...