The invention belongs to the technical field of nano-coating, in particular to an environmentally friendly nano-coating. By weight, the raw materials include: nano-silica 10_22, acrylic acid 7_15, ethyl butenoate 20_30, nano-calcium oxide 5_13, tributyl citrate 1_10, mica 2_8, silica powder 3_9, thickener 0.4_0.8, antioxidant 0.2_0.6. The environmental protection nano-coating of the invention has green composition, environmental protection, excellent acid, alkali, corrosion resistance and mechanical strength, and is suitable for coating automobiles and furniture; the raw material used in the invention has good compatibility with tributyl citrate, excellent cold, light and water resistance, high plasticizing efficiency, and is an environmentally friendly plasticizer; the silica powder has large porosity, strong absorption, and high plasticizing efficiency. Chemical stability, wear resistance, heat resistance and other characteristics can provide excellent surface properties, compatibilization, thickening and adhesion for coatings.
【技术实现步骤摘要】
环保纳米涂层
本专利技术属于纳米涂层
，具体的涉及一种环保纳米涂层。
技术介绍
纳米涂层是指纳米无毒涂层的先进工艺，科技含量高的纳米涂层技术。这种高科技纳米涂层不仅无毒无害，还可以缓慢释放出一种物质，降解室内甲醛、二甲苯等有害物质。随着科技的不断进步和生活水平的不断提高，消费者对生活质量的要求也越来越高。在涂料行业，环保、节能是涂料制备及涂装工艺的发展趋势。三分涂料，七分涂装，对于降低环境影响、保护消费者健康而言，涂装过程的质量保证显得更为关键。为了保证涂装过程的环保节能，不仅要求涂料产品本省环保，而且包括施工环节在内的整个生产供应链都要实现环保化。
技术实现思路
本专利技术的目的在于克服现有技术的不足，提供一种环保纳米涂层，该涂层材料具有优异的耐酸、耐碱、防腐蚀性能和机械性能，成分绿色环保。环保纳米涂层，以重量份数计，原料包括：增稠剂是羧甲基纤维素钠、海藻酸丙二醇酯、羟乙基纤维素或羟丙基甲基纤维素中的一种或多种。防老剂是防老剂AP、防老剂AW、防老剂4010NA、防老剂4030或防老剂DNP中的一种或多种。本专利技术具有以下有益效果：本专利技术的环保纳米涂层，成分绿色环保，具有优异的耐酸、耐碱、防腐蚀性能和机械强度，适合作为汽车、家具的涂层。本专利技术所用原料柠檬酸三丁酯相容性好，耐寒、耐光、耐水性能优良，增塑效率高，是一种环保型的增塑剂；硅石粉具有孔隙率大、吸收性强、化学性质稳定、耐磨、耐热等特点，能为涂料提供优异的表面性能、增容、增稠以及附着力。具体实施方式以下结合实施例对本专利技术作进一步描述。实施例1环保纳米涂层，以重量份数计，原料包括：增稠剂...
【技术保护点】
1.一种环保纳米涂层，其特征在于：按重量份数计，原料包括：
【技术特征摘要】
1.一种环保纳米涂层，其特征在于：按重量份数计，原料包括：2.根据权利要求1所述的环保纳米涂层，其特征在于：增稠剂是羧甲基纤维素钠、海藻酸丙二醇酯、羟乙基纤维素或羟丙基甲...