本发明专利技术涉及一种PS复合材料，复合材料按重量份由以下组分组成：PS为80份‑100份；PTFE为3份‑5份；PPTA纤维为20份‑30份；抗静电母粒为10份‑16份；抗氧剂为0.1份‑0.5份；润滑剂为0.1份‑0.3份；聚对苯二甲酰对苯二胺纤维(PPTA纤维)是经过碳酸酯偶联剂处理后的PPTA纤维。本申请中的PPTA纤维有三个作用：它可以搭建成“网络”，抗静电母粒与“网络”很容易形成导电网络，进一步加强PS复合材料的抗静电性能；它可以提升PS复合材料的拉伸强度、弯曲强度、抗冲击强度；PPTA纤维本身具有一定的阻燃性，它的加入提升了PS复合材料的阻燃性能。

A PS Composite Material

The invention relates to a PS composite material, which is composed of the following components according to weight: PS 80 100; PTFE 3 5; PPTA fiber 20 30; antistatic masterbatch 10 16; antioxidant 0.1 0.5; lubricant 0.1 0.3; polyterephthalamide fiber (PPTA fiber) is a PTA fiber treated by carbonate coupling agent. \u3002 The PPTA fiber in this application has three functions: it can build a \network\. The antistatic masterbatch and the \network\ can easily form a conductive network to further strengthen the antistatic properties of PS composites; it can enhance the tensile strength, flexural strength and impact strength of PS composites; PPTA fiber itself has certain flame retardancy, and its addition improves PS composites. Flame retardant properties.

【技术实现步骤摘要】
一种PS复合材料
本专利技术属于高分子材料领域，特别是指一种PS复合材料。
技术介绍
聚苯乙烯(PS)具有质轻、无毒、无臭，化学稳定性好，且在常温下不溶于一般溶剂，吸水性小等优点。尽管PS的综合性能非常优异，但是在一些特殊的应用领域，对力学性能、抗静电性能、阻燃性能有很高的要求，普通PS不能满足这种要求，这就大大限制了PS复合材料的应用范围。如何提高PS材料的不足，是本领域研发人员所一直致力开发的课题。
技术实现思路
本专利技术的目的是提供一种PS复合材料，以解决现有技术中PS材料在力学性能、抗静电性能及阻燃性能不足的问题。本专利技术是通过以下技术方案实现的：一种PS复合材料，按重量份由以下组分组成：所述PPTA纤维是经过碳酸酯偶联剂处理后的PPTA纤维。所述碳酸酯偶联剂为AC-201。所述抗静电母粒的制备方法为：1)称取一定量的PEEA、EPDM-g-MAH及PS；2)将步骤1)中各物料投入高速搅拌机混合，待混合均匀，放入双螺杆挤出机中挤出造粒，烘干既得抗静电母粒。步骤1)中的PEEA、EPDM-g-MAH、及PS的质量比为(2-6)∶(20-30)∶(200-400)。步骤2)中所述本文档来自技高网...

【技术保护点】
1.一种PS复合材料，其特征在于：按重量份由以下组分组成：

【技术特征摘要】
1.一种PS复合材料，其特征在于：按重量份由以下组分组成：所述PPTA纤维是经过碳酸酯偶联剂处理后的PPTA纤维。2.根据权利要求1所述的PS复合材料，其特征在于：所述碳酸酯偶联剂为AC-201。3.根据权利要求1所述的PS复合材料，其特征在于：所述抗静电母粒的制备方法为：1)称取一定量的PEEA、EPDM-g-MAH及PS；2)将步骤1)中各物料投入高速搅拌机混合，待混合均匀，放入双螺杆挤出机中挤出造粒，烘干既得抗静电母粒。4.根据权利要求3所述的PS复合材料，其...

【专利技术属性】
技术研发人员：吴雅萍，
申请(专利权)人：吴雅萍，
类型：发明
国别省市：浙江,33