The invention discloses a method for dehydrogenation treatment and preheating adjustment before welding of Q890 steel plate. The structural parts are dehydrogenated immediately after each welding, and the next welding is carried out immediately after dehydrogenation treatment. The temperature of dehydrogenation treatment is the preheating temperature before the next welding. The temperature of dehydrogenation treatment is controlled at 250 300 C and the heat preservation time is 2 6 hours. By eliminating hydrogen immediately after each welding, the next pre-welding process is saved, which not only prevents hydrogen-induced cracking after welding, but also saves preheating time and energy consumption.
【技术实现步骤摘要】
Q890钢板焊接消氢处理与焊前预热调整方法
本专利技术涉及一种煤矿液压支架焊接技术，尤其涉及一种Q890钢板焊接消氢处理与焊前预热调整方法。
技术介绍
在液压支架发展过程中，煤矿综采支护向大阻力高强度方向发展，钢板材质由Q460逐步迈向Q890高强钢，预热温度、焊丝匹配、热处理等对焊接性能影响很大，在Q890高强钢板焊接时，当焊缝冷却到一定温度时，焊缝中的扩散氢在某些部位聚集而导致开裂。目前，主要是通过加热炉方式进行预热、保温措施，保证焊接Q890高强板的消氢处理。下一次焊前还需预热工序，时间、电能的消耗高。
技术实现思路
本专利技术的目的是提供一种Q890钢板焊接消氢处理与焊前预热调整方法。本专利技术的目的是通过以下技术方案实现的：本专利技术的Q890钢板焊接消氢处理与焊前预热调整方法，结构件每次焊后立即消氢处理，消氢处理后立即进行下一次焊接，消氢处理的温度为下一次焊接的焊前预热温度。由上述本专利技术提供的技术方案可以看出，本专利技术实施例提供的Q890钢板焊接消氢处理与焊前预热调整方法，通过结构件每次焊后立即消氢处理，节省了下一次焊前预热工序，既防止了焊后氢致裂纹...
【技术保护点】
1.一种Q890钢板焊接消氢处理与焊前预热调整方法，其特征在于，结构件每次焊后立即消氢处理，消氢处理后立即进行下一次焊接，消氢处理的温度为下一次焊接的焊前预热温度。
【技术特征摘要】
1.一种Q890钢板焊接消氢处理与焊前预热调整方法，其特征在于，结构件每次焊后立即消氢处理，消氢处理后立即进行下一次焊接，消氢处理的温度为下一次焊接的...
【专利技术属性】
技术研发人员：刘爱民，刘彩梅，刘国飞，王震，刘超，
申请(专利权)人：中煤北京煤矿机械有限责任公司，
类型：发明
国别省市：北京,11