The invention relates to the technical field of powder coatings, in particular to a water-based coating method of powder coatings, which mixes powder coatings and water evenly, coats on the surface of test plates and solidifies at step temperature. The water-based coating method of the invention takes water as a diluting and dispersing agent, avoids dust pollution and has environmental friendliness; the water-based coating of the invention can be sprayed and brushed, can handle abnormal workpieces, does not leave dead corners, and has good coating effect; the water-based coating process of the invention is simple, the coating efficiency is high, and easy to control, and is conducive to large-scale application.
【技术实现步骤摘要】
一种粉末涂料的水性涂装方法
本专利技术涉及粉末涂料
，更具体而言，涉及一种粉末涂料的水性涂装方法。
技术介绍
粉末涂料是以微细粉末状存在的固体粉末涂料，以粉末状转移到被涂物上，经烘烤熔融、固化从而成膜的涂料。粉末涂料具有涂膜持久的性能，深受用户喜爱。目前粉末涂料主要采用静电粉末喷涂，以具有雾化咀(使涂料雾化)和放电级(发生电量电流)的涂装机使涂料微粒化，对之施加电荷，在电极与被涂物体之间形成电场，利用其静电吸附作用而涂装。静电粉末喷涂法对施工人员的危害很大，即便工作时佩戴防毒面具，在这样的环境下长期工作也会吸入粉末，有形成尘肺的危险；而且环境中粉尘浓度过高还存在粉尘爆炸的风险。另外，由于静电喷涂法是通过带电方式涂装的，故主要应用于金属底材为主的材料涂装，很难使用于其它非导电材料的涂装。
技术实现思路
本专利技术的目的在于提供一种环境友好的、节约原料的粉末涂料的水性涂装方法。为达到上述目的，本专利技术提供的技术方案为：一种粉末涂料的水性涂装方法，包括以下步骤：将粉末涂料和水按照质量比为1:(0.6-1)的比例，加入质量分数为0.5-3%消泡剂，研磨搅拌均匀，通过涂...
【技术保护点】
1.一种粉末涂料的水性涂装方法，其特征在于，包括以下步骤：将粉末涂料和水按照质量比为1:(0.6‑1)的比例，加入质量分数为0.5‑3%消泡剂，研磨搅拌均匀，通过涂膜机将该涂料涂装在试板上，在阶梯温度下进行固化，冷却到室温，粉末涂料水性涂装完成。
【技术特征摘要】
1.一种粉末涂料的水性涂装方法，其特征在于，包括以下步骤：将粉末涂料和水按照质量比为1:(0.6-1)的比例，加入质量分数为0.5-3%消泡剂，研磨搅拌均匀，通过涂膜机将该涂料涂装在试板上，在阶梯温度下进行固化，冷却到室温，粉末涂料水性涂装完成。2.根据权利要求1所述的一种粉末涂料的水性涂装方法，其特征在于：所述粉末涂料包括聚酯树脂型、环氧树脂型、聚酯-环氧混合型、聚氨酯型...
【专利技术属性】
技术研发人员：宋慧平，解文圣，廖洪强，薛芳斌，程芳琴，
申请(专利权)人：山西大学，
类型：发明
国别省市：山西,14